The deformation behavior and formability of gradient nano-grained (GNG) AISI 304 stainless steel in uniaxial and biaxial states were investigated by means of tensile test and small punch test (SPT). The GNG top layer was fabricated on coarse grains (CG) A
【机 构】
：
Jiangsu Key Laboratory of Advanced Food Manufacturing Equipment & Technology, School of Mechanical E
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
The deformation behavior and formability of gradient nano-grained (GNG) AISI 304 stainless steel in uniaxial and biaxial states were investigated by means of tensile test and small punch test (SPT). The GNG top layer was fabricated on coarse grains (CG) AISI 304 by ultrasonic impact treatment. The results showed that the CG substrate could effectively suppress the strain localization of NC in GNG layer, and an approximate linear relationship existed between the thickness of substrate (h) and uniform true strain before necking (εunif). Grain growth of NC was observed at the stress state with high Stress triaxiality T, which led to better ductility of GNG/CG 304 in SPT, as well as similar true strain after the onset of necking (εneck) compared with coarse 304 in tensile test. Ei-values of GNG/CG 304 with different structures were nearly the same at different punch speeds, and good formability of GNG/CG 304 was demonstrated. However, punch speed and microstructure needed to be optimized to avoid much lost of membrane strain region in biaxial stress state.
其他文献
Induction melting was used as a routine method to synthesize Mg23Ni10, Mg22LaNi10 and Mg21La2Ni10 alloys, and followed by a detailed microstructural characterization which included X-ray diffraction (XRD), scanning electron microscopy (SEM) with energy di
A novel gap-plasmon of Fe3O4@Ag core-shell nanoparticles for surface enhanced fluorescence detection of Rhodamine B (RB) was developed.Fe3O4@Ag core-shell nanostructures with Ag shell and Fe3O4 core were synthetized by self-assembled method with the assis
Learning from the process of biominerals formation provides tremendous ideas for developing advanced synthesis techniques.According to the structure formation of tooth enamel,a recombinant amelogenin his-AmelⅩ was designed and constructed.The protein was
Wear-resistant cladding plates consisting of a substrate (Q345 R) and a clad layer (BTW1) were bonded through hot rolling at the temperature of 1 200 ℃ and a rolling speed of 0.5 m/s. The microhardness of the cladding plate was also tested after being hea
The lap joints of Fe-based metallic glass ribbons were carried by resistance spot welding, and the microstructures of spot welds were investigated by X-ray diffraction and transmission electron microscopy. The results indicated that the perfect formations
The influences of nano silica (NS) on the hydration and microstructure development of steam cured cement high volume fly ash (40 wt％, CHVFA) system were investigated. The compressive strength of mortars was tested with different NS dosage from 0 to 4％. Re
Molecular structures of polycarboxylate (PCE) superplasticizer significantly affect the rheological properties of cement paste. Consequently, we employed self-synthesized PCE copolymers with different carboxylic densities to investigate their influence on
The foamed polypropylene (PP) with excellent mechanical and thermal insulating properties was reinforced by blending chlorinated polyethylene (CPE), followed by compression molding foaming in cross-link. The effects of CPE on the foaming behavior, thermal
Mg/Al/Fe layered double hydroxide (MAF-LDH1) was prepared by solvothermal method with the sodium dodecyl sulfate as the template,and the ethanol system was benefit to growth of sample.The nature in the resulting MAF-LDH was investigated by X-ray diffracti
This work focuses on the dynamic rheological behavior of low water-to-binder ratio cement mortars blended with fly ash microspheres (FAM) or silica fume (SF). The initial slump flow of each group has been controlled at similar values by adjusting the supe