在大批量的模锻生产中,有少量锻件存在错移、超厚、氧化皮坑等缺陷需要返修。杆叉类锻件各部的截面积变化悬殊(见图1),当再次整体加热时(指油、煤、煤气加热),往往是截面积
论文部分内容阅读
在大批量的模锻生产中,有少量锻件存在错移、超厚、氧化皮坑等缺陷需要返修。杆叉类锻件各部的截面积变化悬殊(见图1),当再次整体加热时(指油、煤、煤气加热),往往是截面积小的达到始锻温度时,截面积大的尚未达到始锻温度;反之,截面积大的达到始锻温度时,截面积小的则严重过烧,甚至熔断。因此,这类锻件返修加热时,应有别于原始坯料的加热。
In a large number of forging production, there is a small amount of forgings there is a shift, super-thick, oxide pit and other defects need to repair. When the overall heating (referring to oil, coal, gas heating), often cross-sectional area to reach the initial forging temperature, the cross-sectional area has not yet reached the beginning Forging temperature; the other hand, a large cross-sectional area to reach forging temperature, the cross-sectional area of a small serious over-burning, or even blown. Therefore, this type of forgings rework heating, should be different from the original blank heating.
其他文献
当联想、海尔、华为的国际化初步取得一定成就时,曾经被视为中国企业国际化模式代表的TCL却越来越难以走出亏损的泥潭。TCL如何走出国际化困境,实现真正的“鹰之重生”呢?
W
机加工壳体零件时,往往要借助于螺杆来加强支承力(图1)。它不但能增加工件的稳定性,同时又可利用三根顶杆把工件校正。其一端固定在工作台的T形槽内,一端顶着工件的外缘。而
美国磁性材料的 x—光和中子散射专题讨论会(Workshop on“x—Ray & Neurrunscattering from magnetic matenols)和32届磁学与磁性材料年会(32ND AnnualConference on Magne
我厂生产的拖拉机变速滑杆,原测量方法如图下部所示,用球头柱销样板去对,靠两边的缝隙估测,很不精确。现用改装的专用卡尺测里,如图上部所示,槽距L=卡尺读数+8mm,槽距L可精
我厂10t大型冲天炉从1973年以来就一直采用中央送风与侧吹相结合的送风方式进行熔炼,铁水出炉温度在1400℃以上,焦耗为每吨铁水100kg,每小时实际熔化量为13～15t,采用一般冶金
机械加工偏心件的方法很多,图1所示是要求较严的偏心零件,我们采用图2所示的方法,效果较好。这(?)方法简单易行,不需专门机床,对没有精密机床的小企业很适用。步骤如下:取一
D_(w1)电机钢具有磁感高、生产工艺简单、周期短、成本低的优点。该钢种与一般电机钢的区别在于热轧后,冷轧前增加了常化处理工序。当脱碳退火温度选择合理时,材料能
D_ (w
机床定位误差是产生加工误差的主要因素,特别是在精密加工和超精密加工中更是如此。机床定位误差是指机床在规定的加工空间范围内进行定位的误差。影响机床定位误差的主要因
如图1所示,在立式测长仪上测量扁形量具A、B面对外圆D的对称度,既简便又能保证测量精度。需要作一个30×30mm,高度比被测扁形量具直径大10mm的直角体。首先在立式测长仪的平
王东升状告叶永烈1995年5月下旬,一起因陈伯达照片引发的著作权案在北京市中级人民法院开庭审理。这起案件虽然被圈内人士所关注,但开庭那天,除审判员和当事人外,听众却寥寥