Iron-based superconductor,a promising candi-date for high-field applications,has attracted significant attentions.For practical utilization,the superconducting tapes should have high transport critical current density(Jc),low production cost,larger mechan
【机 构】
：
Key Laboratory of Applied Superconductivity,Institute of Electrical Engineering,Chinese Academy of S
论文部分内容阅读
Iron-based superconductor,a promising candi-date for high-field applications,has attracted significant attentions.For practical utilization,the superconducting tapes should have high transport critical current density(Jc),low production cost,larger mechanical strength and good homogeneity.In this study,seven-filament Cu/Ag-sheathed (Ba,K)Fe2As2 tapes were fabricated from round and square wires.It is found that the tapes rolled from square wires have a desirable uniformity of filament deformation and distribution,compared with the ones rol-led from round wires.Moreover,the Jc of tape was obvi-ously improved by using square drawing dies instead of traditional round ones.For the tapes rolled from square wires annealed under ambient and 2 MPa by hot pressing,the transport Jc values reached 1.51 × 104 A·cm-2 and 4.86 × 104 A·cm-2 (4.2 K,10 T),respectively.The deformation process on the cross section of the tapes dur-ing rolling was analyzed by using the powder-flow model.These results indicate a potential application of Cu/Ag(Ba,K)Fe2As2 tapes in high-magnetic-field region.
其他文献
Coaxial FezO3/TiO2 nanotubes (Fe2O3/TiO2 NTs) were prepared by two anodic oxidation processes.The synthesized Fe2O3/TiO2 NTs catalysts showed high photocatalytic activity in heterogeneous photo-Fenton system.With the help of Fe2O3/TiO2 NTs,4-nitrophenol(1
Although Ni-Ti-O nanopores (NPs) can be fabricated by anodization of mechanically polished NiTi alloys,the top disordered layer is difficult to remove thus hindering the functionality of the Ni-Ti-O NPs.In this work,an electropolishing (EP) pretreatment w
The present work introduces a novel γ\'phase-strengthened Ir-W-Al-Th superalloy for ultrahigh-temper-ature applications.First,the as-cast microstructure and phase transformation of Ir-13W-6Al-0.15Th (at％) alloy during solid solution and aging were inves
It is confirmed that the solid solution tempera-ture range to obtain optimal magnetic properties is different for the magnets with different Fe contents,and the corre-lation between magnetic properties and microstructures influenced by solid solution temp
The aim of this study is to develop processing maps based on two models and compare them with con-ventional processing maps.The hyperbolic sinus constitu-tive equation and artificial neural network (ANN)approaches were used in this investigation to predic
High strength titanium alloys suffer from a limited combination of strength and ductility.Considering their microstructure,the coarse β grain is a detrimental factor.In the present study,the effects of hot deformation and annealing treatment on the β grai
The uniaxial tensile deformation behavior of a sandwich-like structural TiNb-NiTi composite was inves-tigated by uniaxial tensile test and in situ high-energy synchrotron X-ray diffraction (SXRD).It is found that below 1.2％ macroscopic strains,the elastic
The microstructure and high-temperature tensile property of a Ti-47Al-2Cr-2Nb alloy fabricated via selec-tive electron beam melting (SEBM) with hatch spacings of 85,100,and 115 μm were systematically investigated.When the hatch spacing increased from 85 t
Ferroelectric lead-free BaTi1-xZrxO3 ceramic powder samples with various compositions (x =0,0.04,0.06) have been synthesized by conventional high-tem-perature solid-state reaction method at 1450 ℃ for 10 h.Influences of Zr doping on the inter-atomic bondi