【摘 要】
：
桓仁县熔炼厂于今年七月兴建了一台1800KVA电炉,采用电极糊打结炉衬代替碳砖。电炉一次安装、送电、生产75硅铁成功。现将本次开炉情况介绍如下。一、炉衬砌筑及电炉参数 1.
论文部分内容阅读
桓仁县熔炼厂于今年七月兴建了一台1800KVA电炉,采用电极糊打结炉衬代替碳砖。电炉一次安装、送电、生产75硅铁成功。现将本次开炉情况介绍如下。一、炉衬砌筑及电炉参数 1.炉衬砌筑电炉砌衬时由于碳砖供不应求,因此采用电极糊打结炉衬。炉衬砌筑大致如下:紧
Huanren County smelter in July this year to build a 1800KVA electric furnace, the use of electrode paste lining furnace lining instead of carbon brick. Electric furnace once installed, power transmission, production of 75 ferrosilicon success. The current situation is now open as follows. First, the lining of the lining and the parameters of the electric furnace 1. Lining lining electric furnace brick lining due to short supply, so the electrode paste knot lining. Lining lining roughly as follows: tight
其他文献
目的：探讨１７ｐＬＯＨ与晚期大肠癌的关系。方法：运用ＳｏｕｔｈｅｒｎＢｌｏｔ和ＲＦＬＰ（ｒｅｓｔｒｉｃｔｉｏｎｆｒａｇｍｅｎｔｌｅｎｇｔｈｐｏｌｙｍｏｒ－ｐｈｉｓｍａｎａｌｙｓｉｓ）法进行分析。结果：１０９例大肠癌的ＲＦＬＰ分析显示，１７ｐＬＯＨ的频率在ＤｕｋｅｓＤ期（９５％）高于ＤｕｋｅｓＡ、Ｂ、Ｃ各期（５４％～６８％），Ｐ＝０．００６；１７ｐＬＯＨ频率在大肠癌远处器官转移组（９５％）高于大肠癌不伴远处器官转移组（Ｐ＝０．００１）；在大肠癌淋巴
ＣＴ引导下周围型肺癌穿刺活检的临床价值评价辽宁省肿瘤医院（１１００４２）放射线科王喜科于波朱丽波罗娅红病理科肖培刘伟ＣＴ引导周围型肺癌介入活检是非手术取材、进行细胞学及组织学检查的最有
由于未来经济上的需要开采杂质含量高的铜矿以及日益严格的环保法的限制,因此,需要对铜熔炼各工艺过程中砷的分配状况进行详细的研究。为此,开发了一个新的综合方法,用来确
近些年来,国外越来越重视含铁废料利用方法的研究。在其它条件均相同的情况下,钢铁厂含铁废料的发生量明显大于利用量,这是由于含铁废料中锌、铅、碱金属这类有害杂质含量高
日本昭和铝公司最近使用由该公司的偏析法生产的99.9%铝锭,生产高压电容器用铝箔获得基本成功。以前,高压电容器用铝箔只能用99.99%的高纯铝,这次昭和铝公司由于已有可能采
本文阐述电炉炼钢能量平衡的基本理论,按照电弧炉运行的电热特性,分析了能量平衡的测试结果。最后,结合目前国内外现代电炉炼钢新技术,着重介绍电炉炼钢设备与工艺二方面的节
一、概况我厂一车间103~#炉是一台容量为1800kVA冶炼硅钙合金的敞口式矿热炉。该炉投产后炉气污染周围环境,为此,我们于1985年着手进行了烟气净化的准备工作。硅钙合金电炉
一、前言炼铁厂高炉出渣用的16.5m~3铸钢渣罐,原材质是ZG25钢。由于渣罐是处在激冷激热状态下工作,渣罐容易变形和开裂,寿命较短。如过去生铁年产量150～160万t,渣罐消耗50～60
康莱特注射液治疗晚期恶性肿瘤３５例疗效分析梁耀君我科于９５年１２月至９７年３月中，试用中药抗癌药物康莱特注射液治疗对手术、放疗、化疗失败或因体质太差难以耐受放、化疗的晚期恶性肿瘤患
上钢一厂为提高高炉利用系数,曾采用煤+油150公斤/吨铁的大喷吹量配合下的富氧操作,取得了较好的效果。但自1980年起,由于能源紧张,高炉停止使用重油,这样,原来喷油时油在风