【摘 要】
：
In order to optimize the dehydriding process for producing nanocrystalline Mg alloy powders by hydriding-dehydriding treatment, nano-structured as-hydrided Mg-3
【机 构】
：
School of Materials Science and Engineering
论文部分内容阅读
In order to optimize the dehydriding process for producing nanocrystalline Mg alloy powders by hydriding-dehydriding treatment, nano-structured as-hydrided Mg-3%Al-1%Zn (AZ31 Mg) (mass fraction) alloy powders were thermally dehydrided at various temperatures from 275 to 375 ℃. The kinetics of hydrogen desorption was examined by hydrogen discharge measurement during dehydriding. The microstructure of the as-hydrided and the subsequently fully dehydrided alloy powders was investigated by X-ray diffraction analysis (XRD) and transmission electron microscopy (TEM), respectively. Both the desorption kinetics and the grain size of the alloy after complete dehydriding were found to be strongly dependent on the processing temperature. The higher the temperature, the faster the desorption, and the more significant the grain growth. When the desorption temperature was raised from 300 to 375 ℃, the time to achieve complete dehydriding was shortened from 190 to 20 min, and the average grain size increased correspondingly from 20 to 58 nm.
其他文献
目的:报告泌尿外科4年内后腹腔镜下肾肿瘤剜除的97例患者肾动脉阻断时间与术后肾功能受损情况。方法:回顾分析2011年7月~2015年3月后腹腔镜肾肿瘤剜除患者97例,肾动脉全阻断
目的:评价腹腔镜膀胱部分切除术治疗膀胱副神经节瘤的疗效。方法:回顾性分析2005年10月~2015年10月12例膀胱副神经节瘤行腹腔镜膀胱部分切除术并得到随访的临床资料。结果:手
NdFe1-xCoxO3(x=0.0-0.5)powders were prepared by a sol-gel citric method.X-ray diffraction was used to confirm the phase composition of the powders.All the sampl
目的:探讨肛管外接冲洗器在膀胱血凝块清除术中的应用价值。方法:回顾性分析安康市中心医院泌尿外科2013年3月~2015年12月及中国人民解放军总医院泌尿外科2016年2月~2016年6
目的:探讨经尿道前列腺剜除术治疗伴尿肌无力(ACD)的前列腺增生症(BPH)的临床疗效。方法:回顾性分析行经尿道前列腺剜除术治疗的36例伴ACD的前列腺增生患者,记录围手术期、术
目的:探讨棒状水囊扩张导管治疗男性尿道狭窄的临床疗效。方法:对收治的36例男性尿道狭窄患者根据狭窄的段长度分组,其中短段组(狭窄长度≤1cm)17例,长段组19例(狭窄长度>1cm
目的:分析穿刺针配合组合式输尿管软镜处理难治性肾下盏结石的安全性及有效性。方法:58例单侧肾下盏结石患者,全身麻醉,取患侧抬高30~35°斜截石位,输尿管软镜找到目标结石,
ZnO nanotubes were hydrothermally synthesized and the ZNTs/CeO2 fluorescent composite were prepared by introducing nano CeO2 particles into ZnO nano-tubes via a
Based on the Miedema model and Extended Miedema theory, the formation energies of different solute components in Er-X binary system and Al-Er-X ternary systems
The oxidation behavior of chemical vapor infiltration (CVI), molten silicon infiltration (MSI) and CVI+MSI C/SiC composites at 500-1 400 ℃ was studied. The oxi