The Li 4SiO 4 has been prepared by the sol gel method and characterized by IR, DTA, TG, XRD, SEM and AC impedance measurements. The results showed that in co
【机 构】
：
河北师范大学化学系!石家庄050016,河北师范大学化学系!石家庄050016,河北师范大学化学系!石家庄050016
论文部分内容阅读
The Li 4SiO 4 has been prepared by the sol gel method and characterized by IR, DTA, TG, XRD, SEM and AC impedance measurements. The results showed that in comparison with the solid state method Li 4SiO 4 could be obtained by sol gel method at lower temperature and the products exhibited smaller particle size and higher ionic conductivity.
The Li 4SiO 4 has been prepared by the sol gel method and characterized by IR, DTA, TG, XRD, SEM and AC impedance measurements. The results was that in comparison with the solid state method Li 4SiO 4 could be obtained by sol gel method at lower temperature and the products found smaller particle size and higher ionic conductivity.
其他文献
用沉淀法制备了 L i3PO4 、Fe PO4 和 5% L i3PO4 ·Fe PO4 3种固体表面材料 ,并用 XRD、IR、TPD和激光促进材料表面反应 ( L SSR)等技术研究了在这些化合物固体表面上甲醇氧
用半微量相平衡方法研究了 Zn SO4 - Val- H2 O体系在 2 5℃时的溶度图及饱和溶液折光率曲线 .体系中未形成新化合物 .合成了配合物 Zn( Val) SO4 · H2 O、Zn( Val) 2 · H2
对 -溴烯丙基苯依次与三乙氧基硅烷加成、二苯膦钾膦化、气相法二氧化硅固载化 ,再与氯化钯反应 ,合成了聚 γ- ( p-二苯膦苯基 )丙基硅氧烷钯 ( )配合物 ,研究了其催化芳基
应用W/O型微乳液法制备了纳米量级包裹型超细铁粉.由XRD、SEM、TEM和IR谱测试表明:它属于表面活性剂包裹型超细微粒.平均粒径约120nm.微粒的密度为3.00g/cm3.比饱和磁化强度
利用吡啶氮烷基化合成了一系列具有空间效应的水溶性和油溶性的四 ( 4 - N-吡啶基 )卟啉衍生物及其对应的金属钴卟啉 ,经元素分析 ,富利叶变换红外光谱 ( FTIR) ,基质辅助激
采用Nd(naph)3-Al(C2H5)3-(t-C4H9)Cl三组分稀土催化剂进行丁二烯(BD)-异戊二烯(IP)的顺式共聚合,在聚合过程中引入有机氯代烃(RCl),以与聚合液中的烷基铝作用生成阳离子活性
采用沉淀法和浸渍法分别制备了ZrO2-Al2O3复合载体和Co-Mo-K耐硫变换催化剂. 研究了ZrO2对Co-Mo-K耐硫变换催化剂活性及热稳定性的影响. 利用XRD、BET、TG、XPS 等手段对催化
在 Mn- Na2 WO4 / Si O2 催化剂上 ,考察了水蒸汽对乙烷氧化脱氢制乙烯反应的影响 ,结果表明加入适量水蒸汽对提高乙烯选择性有利 .在催化剂装量 10 m L,V( C2 H6)∶ V( O2 )
用二次微分简易示波伏安法测定了金刚石酸洗废液中的痕量镍 .结果表明 :在 0 .2 0mol/ L NH4 Ac- 0 .0 0 5mol/ L KNO3- 0 .0 2 %丁二酮肟中 ,Ni2 +浓度在 3× 10 -7～ 3.5× 1
本文通过问卷形式对新疆喀什师范学院语言系,人文系,法政系,教育系,体育系,数学系,物理系和信息工程系等非环境专业的少数民族大学生环境意识,环境知识及生态教育现状作了调