Waste packaging polyethylene (WPE) was used to modify raw asphalt by melt blending the components at 190℃ for 1 h in a simple mixer and subsequently machining them at 120℃ for 1 h in a high-speed shearing machine. The effect of modiifcation on the degree
【机 构】
：
School of Mechanical and Precision Instrument Engineering, Xi’an University of Technology, Xi’an 710
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
Waste packaging polyethylene (WPE) was used to modify raw asphalt by melt blending the components at 190℃ for 1 h in a simple mixer and subsequently machining them at 120℃ for 1 h in a high-speed shearing machine. The effect of modiifcation on the degree of the penetration, the softening point and the ductility of the asphalt was studied using lfuorescent microscopy, infrared spectrometry, component changes and various other techniques. The experimental results showed that no chemical reactions took place in the components themselves (saturate, aromatic, asphaltene and resin) during the modifications. The softening point and penetration of the asphalt were found to be closely related to the resulting contents of the asphaltene, saturate and resin components. In addition, aromatics were identified as having the greatest impact on the ductility of the asphalt.
其他文献
The chloride ion transmission model considering diffusion and convection was established respectively for different zones in concrete by analyzing chloride ion transmission mechanism under the drying-wetting cycles. The finite difference method was adopte
We prepared graphene(GE) with a mean size of 3087 nm. The transition of graphene oxide (GO) to GE was conifrmed by UV-visible spectroscopy, Fourier transform infrared spectroscopy (FTIR) and X-ray diffraction (XRD). The experimental results of optical mic
Our researches are based on the fact that the systems composed of polyacrylamide and montmorillonite under a kind of shear state often appear in some important practical processes like drilling welletc. The viscosity of polyacrylamide is usually the most
The influence of Al content on microstructure characterization and indentation hardness testing behavior of Mg-8Sn-xAl(x=1 wt%, 2 wt%, 3 wt%)-1Zn alloys was investigated by optical microscope, Pandat software, X-ray diffraction, scanning electron microsco
Commercial spherical activated carbon (SAC) was modified by impregnation to enhance the catalytic properties of SAC in acetylene hydrochlorination through melamine modification. Different modification conditions for SAC with nitrogen were compared by chan
We investigated the effect of structural factor and amide grafted multi-walled carbon nanotubes (MWNTs-NH2) on crushing characteristics of filament wound CFRP tube under quasi-static compression conditon. It was found that CFRP tubes sequentially showed t
Carbon fibers (CFs) were coated with a nickel-phosphorus (Ni-P) film using an electroless plating process. The morphology, elemental composition and phases in the coating layer of the CFs were investigated by scanning electron microscopy (SEM), energy dis