[期刊论文] 作者：ZHOU Jicheng YAN Jianwu TIAN L,
来源：武汉理工大学学报：材料科学英文版 年份：2007
Nanoscale thick amorphous Ni-Cr alloy thin films were fabricated by low-energy ion beam sputtering technology:then the as-deposited samples experienced rapi...
[期刊论文] 作者：ZHOU Jicheng,YAN Jianwu,TIAN L,
来源：武汉理工大学学报(材料科学版) 年份：2007
Nanoscale thick amorphous Ni-Cr alloy thin films were fabricated by low-energy ion beam sputtering technology; then the as-deposited samples experienced rapid t...
[期刊论文] 作者：WANG Chenxi,LIANG Wei,YAN Jianwu,JIN Zhao,ZHANG Weibin,LI Xiaofei,
来源：地理学报（英文版） 年份：2022
With the implementation of the Grain for Green Project,vegetation cover has expe-rienced great changes throughout the Loess Plateau (LP).These changes substantially in-fluence the intensity of evapotranspiration (ET),thereby regulating the ......
[会议论文] 作者：Zou Bingmei,Yan Jianwu,Peng Xiaohua,Luo Lihua,邹冰梅,阎建武,彭晓华,罗利华,
来源：2012年全国炼钢-连铸生产技术会 年份：2012
异形坯的质量缺陷分表面缺陷、内部缺陷和形状缺陷。表面缺陷主要是钢液在结晶器内凝固成坯壳的过程中产生的，主要有表面纵裂、角部纵裂、表面横裂、星形裂纹、表面夹渣、......
[会议论文] 作者：Zou Bingmei,邹冰梅,Yan Jianwu,阎建武,Peng Xiaohua,彭晓华,Luo Lihua,罗利华,
来源：2012年全国炼钢-连铸生产技术会 年份：2012
异形坯的质量缺陷分表面缺陷、内部缺陷和形状缺陷。表面缺陷主要是钢液在结晶器内凝固成坯壳的过程中产生的，主要有表面纵裂、角部纵裂、表面横裂、星形裂纹、表面夹渣、凹坑和气孔。内部缺陷主要与钢水中S、P含量过高、二次冷却水分配不合理、支撑系统没严格对......
[会议论文] 作者：Chen Jiang,Liu Zhipeng,Feng Ke,Long Hao,陈将,刘志鹏,冯科,龙灏,Zeng Shan,Yan Jianwu,Li Yulin,曾珊,阎建武,李宇林,
来源：2012年全国炼钢-连铸生产技术会 年份：2012
针对三铰点轻压下水平扇形段的结构特点，本文介绍了该扇形段标定方法，用测试的方法确定了最小的标定力。通过对测试数据的分析，找到了一种辊缝补偿的方法，并且用试验测试的方......
[会议论文] 作者：Chen Jiang,陈将,Zeng Shan,曾珊,Liu Zhipeng,刘志鹏,Yan Jianwu,阎建武,Feng Ke,冯科,Long Hao,龙灏,Li Yulin,李宇林,
来源：2012年全国炼钢-连铸生产技术会 年份：2012
针对三铰点轻压下水平扇形段的结构特点，本文介绍了该扇形段标定方法，用测试的方法确定了最小的标定力。通过对测试数据的分析，找到了一种辊缝补偿的方法，并且用试验测试的方法验证了其合理性。......