stresscorrosioncracking相关论文
Effect of sulfate-reducing bacteria on hydrogen permeation and stress corrosion cracking behavior of
980 high-strength steel has been widely used in marine engineering structures due to its high strength and toughness.How......
Effect of cathodic potential on stress corrosion cracking behavior of 21Cr2NiMo steel in simulated s
This study aims at providing systematically insights to clarify the impact of cathodic polarization on the stress corros......
Effect of Cl- Concentration on the SCC Behavior of 13Cr Stainless Steel in High-Pressure CO2 Environ
An effect of Cl-concentration on the stress corrosion cracking (SCC) behavior of 13Cr stainless steel was investigated b......
In high sour gas reservoir drilling process, it happens occasionally that high-strength drill pipe suffers brittle fract......
Effects of Aging Treatment on Intergranular Corrosion and Stress Corrosion Cracking Behavior of AA70
In order to study the effects of aging treatment on the intergranular corrosion(IGC)and stress corrosion cracking(SCC)of......
Slow strain rate testing (SSRT) was employed to study the stress corrosion cracking (SCC) behavior of ZE41 magnesium all......
...
Recently,dissimilar materials welding hasbeen increasingly considered in industry because of its severalbenefits includi......
Effect of Micro-mechanical State at Tip of Stress Corrosion Cracking on Crack Growth in Safety-end W
It is one of the main failure and degradation forms that the stress corrosion cracking (SCC) of austenitic stainless ste......
文章介绍某反应釜内盘管使用仅数月即发生多处泄漏质量问题,经补焊修复后,但泄漏仍时有发生,通过对存在泄漏问题的盘管进行宏观检......
Distribution of hardness,grain boundary chemistry,types of grain boundary and fraction,local deformation and stress corr......
Analyzed Approach of Mechanical State at the tip of Stress Corrosion Cracking Based on Elastic-Plast
The mechanical state at the tip of stress corrosion cracking(SCC)is one of the key factors affecting SCC behavior.Althou......
Effects of Zn injection on the stress corrosion cracking behavior of sensitized stainless steel in b
Stress corrosion cracking(SCC)of sensitized 304 stainless steel(SS)in borated and lithiated high temperature water witho......
Stress Corrosion Cracking Behavior of Dissimilar Metal Weld A508/52M in High Temperature Water Envir
The stress corrosion cracking(SCC)behavior f A508/52M part in dissimilar metal weld A508/52M/316L in simulated primary w......
The Effect of Aging Temperature on Cast Austenitic Stainless Steel in Simulated BWR Coolant Conditio
Stress corrosion cracking (SCC) susceptibility of aged CF8A cast austenitic stainless steels (CASS)with different ferrit......
本文介绍新型高镍合金钢,一种超级奥氏体不锈钢NAS254N( SUS836L、UNS S32053)的特性以及在化工设备和压力容器领域里的应用情况.......
本文研究了7136 Al合金T6、T79和T74态的组织、力学性能和应力腐蚀开裂(SCC)之间的关系,讨论了组织对力学性能和腐蚀开裂敏感性的......
Stress corrosion cracking(SCC)is an inherently complicated material degradation induced by combinations of material,......
通过应力腐蚀开裂测试、晶间腐蚀测试实验结合扫描电镜以及高角度环形暗场像扫描透射电镜观测,研究Al-Zn-Mg-Cu合金中腐蚀行为、晶......
The stress corrosion cracking (SCC) behaviors of 2A12 aluminum alloy after annealing treatment were studied by slow stra......
ＦＣＣ系统中重沸器破裂原因分析鱼济陈刚卢润之毕志民兰州炼油化工总厂７３００６０在１９８４年至１９８５年期间，兰州炼油厂两套催化裂化（ＦＣＣ）和气体精馏装置１６ＭｎＲ钢制重沸器在......