TUNDISH相关论文
Bubble defect is one of the main defects of an automobile sheet.To solve this defect,the technology for nitrogen-argon m......
中间包内钢水在自由流出过程中容易产生汇流漩涡。汇流漩涡会引起空气和钢渣的吸入,降低钢水质量。中间包内通常设有塞棒、挡墙等......
通过预先制定的检验方案,将盘条的化学成分作为唯一的对比基准,对比了盘条与对应不同时间段的中间包钢液及盘条与对应钢坯的C,Si,M......
In the water modeling experiments, three cases were considered, i.e. , a bare tundish, a tundish equipped with a turbule......
介绍了连铸中间包透气上水口的性能和种类及连铸工艺对透气上水口性能的要求。利用合成莫来石颗粒、α-Al2O3细粉及特殊结合剂研制......
高效的利用连铸生产设备的能力是炼钢—连铸生产计划优化技术的主要目标。在描述了炼钢—连铸生产计划调度编制步骤的基础上,重点......
Effect of Thermal Buoyancy on Fluid Flow and Inclusion Motion in Tundish without Flow Control Device
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生......
Fluid flow and mixing of molten steel in a twin-slab-strand continuous casting tundish were investigated using a mixing ......
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生......
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生......
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生......
Application of Computational Fluid Dynamics to analysis of metallurgical process for continuous cast
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生......
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生......
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生......
Numerical investigation of the effect of transitory strand opening on mixing in a multistrand tundis
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生......
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生......
Improvement of tundish shape and optimization of flow control devices for sequence casting heavy ste
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生......
Effect of Thermal Buoyancy on Fluid Flow and Inclusion Motion in Tundish without Flow Control Device
The κ-ε two-equation model is used to simulate the fluid flow in the continuous casting tundish coupling with the effe......
Carbon-free basic dry vibration mix was prepared using middle grade magnesia and fused magnesia as main starting materia......
To enhance the service life of magnesia based slag dam,composite slag dam was designed to be cast with alumina magnesia ......
Much researches on the operation and structure of tundish were carried out at Xiangtan Iron and Steel Co Ltd to increase......
结合整体稳流器在连铸中间包上的应用特点，探讨了两种结构形式的整体稳流器对钢液流动状态的影响，并阐述了整体稳流器在中间包上的结......
...
Numerical investigation of the effect of transitory strand opening on mixing in a multistrand tundis
In a multistrand,the outlet near the inlet produces short circuiting flow.This leads to the formation of dead zones insi......
Improvement of tundish shape and optimization of flow control devices for sequence casting heavy ste
The metallurgical effect of a round tundish used to cast heavy steel ingots in machine works at present was evaluated th......
Application of Computational Fluid Dynamics to analysis of metallurgical process for continuous cast
A series of simulations by mathematical and physical modeling on fluid flow, mass and heat transfer in continuous castin......
The configuration of the tundish for a two-strand horizontal continuous caster was designed and optimized through water ......
中间包配置感应加热器后的结构与原型中间包结构差异较大,不宜使用常规添加挡墙、挡坝或稳流器的方式优化流场。针对国内典型5流通......
结合某公司双冲击点板坯中间包生产现状,利用水模实验对中间包内钢水流动特性进行了研究.结果表明：原中间包结构存在明显的短路流,......
连铸中间包用干式振动料是继无工作衬、绝热板、涂抹料后的第四代中间包工作衬,起着精炼钢水、洁净钢水和去除非金属夹杂等作用,具......
通过改进方坯连铸机预热装置管路结构、优化管路材质、合理布置烧嘴位置、改进烧嘴的密封法兰、缩小中间罐盖的浸入孔尺寸,改善了......
梅山炼钢厂通过对中间包的扩容改造,提高中间包及水口的烘烤效率;增加中间包冶金稳流器,改进中间包水口座砖、挡渣墙等耐火材质;进......
介绍韶钢炼轧厂中间包定径水口快速在线更换技术的应用、效果及其存在的问题．...
原型中间包结构不合理，两个水口进出口温差不一致，且包内温降较大．优化后中间包温度分布更加合理，进出口温差减小，最低温度有所提高，尤其......
以国内某钢厂板坯连铸中间包为原型，进行控流装置的物理和数值模拟优化，提出优化方案．对比物理模拟和数值模拟结果发现，对于不使用抑湍......
根据相似原理,建立1∶3的物理模拟模型,通过正交试验考察了挡渣堰、导流坝组合控流装置对中间包流场的影响。研究结果表明,堰坝间......
通过两流板坯中间包水模实验,研究了抑湍器以及不同控流装置的组合对中间包流动特性的影响.结果表明,合理使用抑湍器能延长开始响......
利用一维稳态传热模型，计算中间包底面温度，建立了底面温度与中间包衬里损伤程度问的对应关系，发现中间包底面温度随着衬里损伤程度增......
采用数值模型方法对太钢第三炼钢厂板坯连铸用中间包内部结构几何参数进行了最优化虚拟实验研究,研究中使用的评价指标是钢液在中......
以FTSC双效冲击板加单坝结构的中间包为研究对象，应用FLUENT软件计算了中间包的三维流场、温度场、夹杂物运动轨迹及不同尺寸夹杂物......
在专门设计的二维模型上对非等温流现象的形成条件进行了实验研究，定义了衡量非等温流动出现的准数，并给出了临界值，以用来判断中间包......
为了延长钢水在中间包内的停留时间、减少卷渣和改善夹杂物的上浮排出，提高铸坯的质量，通过对中间包结构发展的分析，提出了新型中间包......
文章就钢中三氧化二铝产生的原因、上浮机理及其影响其排除因素进行了分析,并提出保证铝镇静钢顺利浇注的一些技术措施.......
为使天钢六流方坯连铸中间包内钢液流动特性更加合理，采用水力学物理模拟实验，研究了导流孔距底部距离为110、80、60、30mm时钢液流......
采用VOF模型模拟气泡在钢液中的运动过程，根据计算结果研究气泡的运动特性。结果表明，气泡外形由初始时的球形变为心形，而后逐渐变为......
根据某厂实际中间包的操作工艺参数，采用欧拉两流体模型和拉格郎日随机轨道模型，模拟计算采用湍流控制器和气幕挡墙技术的中间包内的......
采用不同性能参数的多孔透气砖进行中间包底部吹气水模实验，研究透气砖的气孔率、透气度、平均孔径对所形成的气泡大小和能形成有效......
采用水模拟试验研究湍流抑制器对中间包钢液流动特性的影响。结果表明,拉速变化时单层湍流抑制器对钢液流动影响程度较小,双层湍流......
中间包是连铸机中一个重要的冶金反应器,中间包内钢液流动行为直接影响着连铸坯的质量。因此,十分有必要利用水力学模型研究湍流控......