【摘 要】
:
研究稀土Ce元素对HMn64-8-5-1.5合金的组织和力学性能的影响.结果表明:添加Ce元素可以细化铸态和热挤压态HMn64-8-5-1.5合金的基体晶粒,同时减少大块硬质相的尺寸和数量,促进细小的Mn5Si3硬质相析出;硬质相在受拉应力时产生裂纹源,添加稀土Ce增加硬质相数量,进而产生更多的裂纹源,降低HMn64-8-5-1.5合金的力学性能.
【出 处】
:
第六届海内外中华青年材料科学技术研讨会暨第十五届全国青年材料科学技术研讨会
论文部分内容阅读
研究稀土Ce元素对HMn64-8-5-1.5合金的组织和力学性能的影响.结果表明:添加Ce元素可以细化铸态和热挤压态HMn64-8-5-1.5合金的基体晶粒,同时减少大块硬质相的尺寸和数量,促进细小的Mn5Si3硬质相析出;硬质相在受拉应力时产生裂纹源,添加稀土Ce增加硬质相数量,进而产生更多的裂纹源,降低HMn64-8-5-1.5合金的力学性能.
其他文献
Half-Heusler(HH)compounds are important high temperature thermoelectric(TE)materials having attracted considerable attention in the recent years.High figure of merit zT values of 0.8~1.0 have been obt
As a family of promising thermoelectric materials,the BiCuSeO oxyselenides have recently acquired ever-increasing attention thus being extensively studied.The figure of merit ZT of the BiCuSeO-based t
Lead chalcogenides are dominant thermoelectric materials in the medium-temperature range,owing to their highly favorable electronic band structures and low thermal conductivities achievable.An importa
Lead-free SnTe compound shows promising good thermoelectric performance.However,stoichiometric SnTe is a strongly p-type semiconductor with a carrier concentration of about 1×1020 cm-3,which correspon
SbCrSe3 has a unique quasi-one-dimensional structure in which two parallel chains of CrSe6 octahedra are linked by antimony atoms to form the pseudo one dimensional crystal structure.Such quasi-one-di
Low lattice thermal conductivity(L)is a key parameter for high efficient thermoelectric materials.There are generally several strategies for low L,such as stronger low sound velocity,phonon-phonon int
Antimony telluride(Sb2Te3)and its based alloys are of importance p-type semiconductors for the thermoelectric applications near room temperature.Herein,we report a simple,low-energy intensive and scal
本文研究了固溶处理对7A52/7B52铝合金叠层板力学性能和断裂行为的影响.采用力学拉伸实验、夏比冲击实验测试了叠层板的力学性能.采用扫描电子显微镜(SEM)和电子背散射衍射(EBSD)研究了平均晶粒尺寸、再结晶晶界比例及断口形貌等微观组织特征和断裂行为的关系.建立了固溶处理与力学性能和断裂行为的联系.结果表明,经过475℃/1h固溶后,7B52合金回溶效果较好,抗拉强度(Rm)为659MPa,延
Lead chalcogenides are the most efficient thermoelectric materials.In comparison,SnTe,a lead-free analogue of PbTe,exhibits inferior thermoelectric performance due to low Seebeck coefficient and high
The layered MnSb2Se4 monoclinic phase material was reported to be a narrow band semiconductor having large Seebeck coefficient,intrinsically low thermal conductivity,but humbled thermoelectric zT valu