【摘 要】
：
Based on the previous research, the researchers select a group of iron phosphate glasses(38%Fe2O3-51%P2O5-6.4%CaO-4.5%ZrO2 wt%, Y1) with good alkali-resistant performance, and compare them with conven
【机 构】
：
School of Materials Science and Engineering,University of Jinan,Jinan,China
【出 处】
：
第二届中国国际复合材料科技大会 (CCCM-2)
论文部分内容阅读
Based on the previous research, the researchers select a group of iron phosphate glasses(38%Fe2O3-51%P2O5-6.4%CaO-4.5%ZrO2 wt%, Y1) with good alkali-resistant performance, and compare them with conventional fiber glasses(E glass, Y2, boron-free and fluoride-free glass, Y3, Alkali-resistant glass, Y4) to explore the feasibility of producing alkali glass fiber with iron phosphate glass.
其他文献
In this study, a partial graphitic hierarchical porous carbon nanofiber (PGHPCNF) is prepared via eletrospinning followed by pyrolysis, KOH activation and acid treatment.The as-obtained carbon nanofib
A high-yield porous graphene/carbon nanowire (PG/CNW) composite is synthesized via in-situ chemical oxidative polymerization followed by carbonization and KOH activation.An easy and efficient vacuum-a
Glass transition temperature (Tg) of epoxy resin composites reinforced by amino groups (-NH2) and carboxyl groups (-COOH) grafted carbon nanotubes (CNTs) were investigated, respectively, and compared
A novel magnetic multi walled carbon nanotubes with fluorescent imaging performance (F&M-MWCNTs) was successfully fabricated by combining in situ atom transfer radical polymerization (ATRP) and fluore
The eco-friendly and renewable polymers (poly(dopamine) and hydroxyethyl cellulose) were used as modifiers to enhance dispersibility of short carbon fibers (SCFs) in water-based solution.The dispersio
In this study, AZ31B magnesium alloy was treated by different kinds of silanes, including γ-(2,3-epoxypropoxy) propyltrimethoxysilane (KH-560), γ-(methacryloxy) propyltrimethoxysilane (KH-570), N-(2-a
Aluminoborosilicate glasses with different CaO/La2O3 ratio were prepared by conventional melt quenching method.The structure were investigated by FTIR.The thermal property was always measured by DSC.T
An active composite is a type of an active material without the usage of any functional material such as shape memory alloy or piezoelectric material, but its shape can be changed during the thermal a
The results of work on the development of abrasive superhard composite materials based on diamond and cubic boron nitride due to structuring the powder material by carbon binder at subatmospheric pres
In order to figure out effects of alkaline-earth metal oxides on iron phosphate glass structure and properties, the glass system (100-x) (60P2O5-40Fe2O3)-xRO (RO=MgO, CaO, SrO, x=0,5,10,15,20,25 mol%)