Graded CrN film and multilayer Cr/CrN films with different modulate periods were synthesized on bearing steels by controlled arc ion plating, and the influe
【机 构】
：
Science and Technology on Power Beam Processes Laboratory,Beijing Aeronautical Manufacturing Technol
【出 处】
：
2014国际高能束与特种能场制造暨第五届高能束流加工技术国际学术会议
论文部分内容阅读
Graded CrN film and multilayer Cr/CrN films with different modulate periods were synthesized on bearing steels by controlled arc ion plating, and the influences of layer structure and modulus on mechanical properties of Cr/CrN films were investigated.The thickness and morphology of films were observed by scanning electronic microscope (SEM).Composition analysis of the films was carried out by energy dispersive spectroscopy (EDS) in SEM.Structure was investigated by X-ray diffraction (XRD).Mechanical properties were evaluated using nano-indentation and scratch tester.The results showed that the thickness of films with different structure and modulus was around 6 μm, main orientations of CrN (111) and (200) presented in Cr/CrN films.The mechanical properties including hardness, modulus, plasticity and adhesion were sensitive to the modulate periods and layer structure, and were obviously improved by the graded layer structure.All of the performances indicated that graded structure of CrN film results in improvement of mechanical properties.
其他文献
高能束流加工技术在现代工业制造领域发挥着越来越大的作用，而涂层制备技术是高能束流加工的技术优势之一。本文通过典型实例，介绍航空发动机先进涂层技术及其应用进展，重点
针对传统热喷涂涂层在服役过程中容易发生剥落失效的问题，本文利用电子束毛化工艺对喷涂前基体表面进行造型加工，之后利用等离子喷涂工艺在具有造型的表面上沉积制备涂层。
采用电子束高频扫描技术对TC4钛合金表面进行处理。分别调整扫描次数、扫描频率、束流等工艺参数，将经过不同工艺处理的TC4钛合金，分别检测了表面硬度、表面组织、硬化层深
飞秒激光由于其极高的光场强度、快速的加工过程，在微纳结构、器件的制作，工业生产领域都有着越来越广泛地应用。单束飞秒激光诱导周期性表面微纳结构是最近发现的一个很有
The main aim of our project was to find tailor acoustically active liposome-based microbubbles efficient for nucleic acids (NA) transfer.Our challenge was t
激光喷丸技术(LSP)是一种新型的表面处理技术，它可以引入深的残余压应力层来改善其力学行为如疲劳寿命以及塑性.块状非晶合金(BMGs)由于其高强度和高硬度，被期望能用于功能
采用大气等离子喷涂技术在2Cr1 3不锈钢基体上沉积了3 mm厚NiCrBSi涂层,并采用等离子焰流对喷涂态涂层进行了重熔处理.利用X射线衍射、扫描电镜和能谱仪对涂层物相、微观
为了提高2Cr13马氏体不锈钢的表面硬度和耐磨、耐冲蚀性,本文利用等离子喷涂技术和重熔工艺在2Crl3马氏体不锈钢表面制备CoCrBSi自熔性高温合金涂层,涂层厚度约为4mm.利
Multilayered Ti/TiN thick films with 10 μ m thickness were deposited by vacuum arc deposition method using a combination of a Ti target and an Ar/N2 mixtur
采用Nd∶ YAG激光器对硬质合金YG8的表面进行激光冲击强化，采用透射电子显微镜观察其近表面微观组织变化，测量冲击前后的表面显微硬度变化，用摩擦磨损试验机对激光冲击试样