Potential-induced-degradation (PID) is one of the major technical challenges to the current PV industry, but the community still lacks a fundamental understanding of this phenomenon.In this study we p
【出 处】
:
SNEC 第九届(2015)国际太阳能产业及光伏工程(上海)论坛
论文部分内容阅读
Potential-induced-degradation (PID) is one of the major technical challenges to the current PV industry, but the community still lacks a fundamental understanding of this phenomenon.In this study we present efforts to better understand the mechanism and root cause of PID, in search of a 100% reliable solution to the problem.We critically evaluate the currently popular theory of sodium ion migration and study the contribution of other captions, as well as the impact of volume resistivity of module materials on PID.
其他文献
In CulnGaSe (CIGS) solar cell industry, ZnO-based transparent conductive electrodes (TCEs) have been mainly studied as window layers because of its low material costs, low-temperature process ability,
In recent years, the phenomenon of snail trails on the surface of PV modules has become a widespread problem encountered by a large number of module makers and solar farms around the world.Previously,
The impact of backsheets and encapsulants on module durability has been studied to a great extent, but the role of metallization pastes is much less understood.We are introducing our initiative to bet
During the last years several PID based module degradations have been reported for existing solar parks.This has caused intensive research activities worldwide to avoid this kind of power losses.Techn
该文公布了自2006年以来,在广州中山大学太阳能系统研究所安装的6种组件系统的发电量及性能.该文涉及的组件技术包括单晶硅、多晶硅、非晶硅、铜铟镓硒、碲化镉和HIT,这些组件均以统一倾角和朝向安装,为广州地区最佳安装角度.通过长期监测发现薄膜组件发电量高于晶体硅组件,而且单晶硅组件的发电优势随着时间推移而降低,2013年全年发电量为707kwh/kWp,与此同时多晶硅组件年发电量为825 kwh/k
Achieving the highest efficiency for c-Si based photovoltaics will require improved light management as substrates thin and surface passivation improves.Nanophotonic structures, structures smaller tha
Electrically conductive adhesive (ECA) materials have been widely used in electronics because of their low curing temperatures resulting in low thermal stresses and their ROHS-compliance.In PV,solder
衬底温度对非晶硅薄膜的生长以及异质结电池中晶体硅表面钝化起到至关重要的作用。实验中采用等离子体增强化学气相沉积技术,在晶体硅表面双面沉积本征氢化非晶硅薄膜,采用等离体增强化学气相沉积技术制备了具有不同微结构、异质结界面形貌等特征的氢化非晶硅薄膜。
During the production of photovoltaic (PV) Si solar panels, a high level of residual stress in Si crystals often remains undetected far into the fabrication process, until ultimately the end product (
Today photovoltaic module manufacturers have a wide choice of different types of back sheets available to them, each exhibiting a specific combination of performance attributes.The latter depend on th