【摘 要】
：
Layered LiNi1/3Co1/3Mn1/3O2 was synthesized by co-precipitation method, and a series of LiNi1/3Co1/3Mn1/3O2/C composites were then prepared by Citric acid, on the surface of LiNi1/3Co1/3Mn1/3O2 using
【机 构】
：
School of Chemistry and Chemical Engineering, Shenzhen University, Shenzhen, 518060
【出 处】
：
2014中国溶胶-凝胶学术研讨会暨国际论坛
论文部分内容阅读
Layered LiNi1/3Co1/3Mn1/3O2 was synthesized by co-precipitation method, and a series of LiNi1/3Co1/3Mn1/3O2/C composites were then prepared by Citric acid, on the surface of LiNi1/3Co1/3Mn1/3O2 using so1-gel method.The bare and composites were characterized by scanning electron microscopy(SEM), transmission electron microscopy(TEM) and X-ray diffraction(XRD).The electrochemical properties of the composites were investigated with galvanostatic charge-discharge test and AC impedance techniques.The results show that the carbon coating did not alter the crystal structure of the LiNi1/3Co1/3Mn1/3O2.The composite 5.0 vt% C-LiNi1/3Co1/3Mn1/3O2 exhibits a good electrochemical performance, its first discharge capacity is 174.2 mAh/g at 0.1C rate and voltage limits of 2.8-4.6V, compare to 156.7 mAh/g of the bare sample.
其他文献
本文采用溶胶-凝胶法制备得到同时具有超疏水性能和高透过率的SiO2减反膜.将适量的六甲基二硅氮烷(HMDS)添加到碱性催化的二氧化硅溶胶中，得到HMDS改性溶胶.使用浸渍-提拉法在基底上镀出的薄膜同时具有超疏水性能和高透过率.薄膜的性能可以由傅里叶变换红外光谱仪、UV-Vis-NIR分光光度计、Film Wizard 32膜系设计软件和接触角测试仪进行测量.实验结果表明：当HMDS与TEOS的摩尔
本文采用乳液聚合方式对聚合物单体苯乙烯进行聚合反应，制备了具有良好的单分散性的聚苯乙烯微球。同时，选用一定浓度的硝酸镍水溶液作为离子源，并加入稳定剂柠檬酸钠，搅拌均匀，形成均一、稳定的溶胶混合液。在此基础上，缓慢加入正己烷溶剂使其与上述溶胶混合液，形成互不相溶的油-水界面。然后极其缓慢的滴加适量的乙醇，通过油-水界面自组装方法得到了单层紧密排列的蛋白结构的氢氧化镍薄膜。通过提拉法将其转移到SiO2
In this paper, the xLiFePO4.yLi3V2(PO4)3/C composite cathode materials were prepared via sol-gel method in order to combine the outstanding performance of LiFePO4 and Li3V2(PO4)3, in which analytic gr
以甲基丙烯酰氧基丙基(甲基)二甲氧基硅烷和甲基三乙氧基硅烷(M为原料,经预水解制备了聚硅氧烷低聚物,与甲基丙烯酰氧基丙基三甲氧基硅烷(MPS)改性硅溶胶复合,以氨丙基三乙氧基硅烷(APS)为固化剂,制备了聚硅氧烷/SiO2透明涂层.采用红外光谱、热重力分析、纳米压痕仪和铅笔硬度表征了涂层的结构和机械性能.研究了MPS/SiO2比例、胶体SiO2含量、APS用量、膜厚和固化工艺条件对杂化涂层结构和性
To modify the oxidative-resistantability of carbon fiber reinforced carbon aerogelthermal insulators, Si-C-Oprecursor sol was prepared with dimethyldiethoxylsilane (DMDES) and methyltrimethoxysilane (
采用过氧钼酸溶胶-凝胶体系首先在SiC颗粒表面包覆MoO3涂层,然后氢气两步还原得到Mo涂层,研究了溶胶-凝胶工艺对MoO3包覆完整性的影响及还原后Mo涂层的成分和形貌；然后,选取Mo包覆SiC粉和Cu粉,采用热压烧结工艺制备了SiCp/Cu复合材料,重点对比分析了Mo界面阻挡层对复合材料导热性能的影响.结果表明：SiC表面丙酮和氢氟酸预清洗处理有利于MoO3涂层的沉积生长；当SiC/MoO3=5
以高锰酸钾为氧化剂,浓硫酸和浓硝酸混合配制的混酸作为反应环境,对PAM型碳纤维进行表面改性,然后以改性碳纤维作为经线和纬线织造成织物,经分切得到的一定宽度的基带,接着通过静电吸附上质量分数0.5-3％的碳粉,最终制成改性碳纤维色带.通过红外(FT-IR),x射线衍射(XRD),扫描电子显微镜(SEM)表征了改性前后的纤维特性变化；分别利用Printronix p7010和Printronix p7
本文在不添加还原剂情况下，以PVP为保护剂采用亚临界水热还原制备水溶性纳米银溶胶，并通过UV-Vis光谱实验探索了前驱体、PVP含量、水热反应时间等因素对制备纳米银溶胶的影响.结果表明：[Ag(NH3)2]OH络合离子水溶液是制备纳米银溶胶的高效前驱体；亚临界状态下可有效激发PVP分子中氮原子和氧原子上的孤对电子产生自由电子促使前驱体中Ag+的还原；PVP可有效阻止银粒子间的团聚，当水热反应时间为
Graphic and iron powders natural micro-alloyed with Ti and V elements were processed by mechanical milling process.The effects of C concentrations and milling processing parameters on powder particle
研究了以恒电流微弧氧化的方式在TC4钛合金表面制备多孔生物陶瓷层的较佳工艺和性能.利用响应曲面设计对恒电流微弧氧化各工艺参数进行设计,利用粗糙度仪、显微硬度仪、X射线衍射仪、扫描电镜等仪器分析检测了膜层的粗糙度、显微硬度、物相组成和表面形貌.讨论了在不同工艺参数下获得膜层的各种性能变化.研究结果表明：当Ca/P为1,正向电流为3A,时间为15min,频率为317.32Hz时,恒电流微弧氧化制备的多