Optimization of Structure Design Parameters and Mechanical Properties of Mg-Al-Ti Composite Sheets F

来源 :第二届中国国际复合材料科技大会 (CCCM-2) | 被引量 : 0次 | 上传用户:liujing6633
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
  The Mg-Al-Ti laminated metal composite sheet combines the advantages of high strength of Ti, light weight, easy melt and atomization of Mg, and good space adaptability of Al.It is well suited to as bumper sheet of Whipple shield structure for space debris shield.The Mg-Al-Ti three layer composite sheet was fabricated by hot roll bonding technology.
其他文献
The ternary layered MAX-phase materials combining the merits of both metals and ceramics are considered as the candidate material for fusion reactor.The different ion beam produced by a tandem acceler
会议
本文采用电沉积的方法将Hummers法制备的氧化石墨烯(G0)还原沉积在金属泡沫镍基底上制备出具有三维介孔结构的还原氧化石墨烯(rGO),并通过第二次电沉积将一层超薄MoO2沉积在rGO表面,形成了具有特殊形貌的MoO2/rGO/Ni超级电容器纳米复合电极材料。
会议
本文以中间相炭微球和硅粉为原料,通过模压反应烧结法获得一种新型多孔SiCf/SiC复合材料。通过改变原料比、球磨时间、炉内压力等研究了多孔材料的微观形貌、力学性能、孔隙率及孔径分布。结果 表明,增加原料的球磨时间,多孔材料的力学性能大幅度提高,孔隙率及孔径分布下降。
以国产高纯石墨为基体,一甲基三氯硅烷为先驱体原料,使用化学气相沉积工艺制备了SiC涂层。利用SEM和XRD分别对筒式工装和笼式工装中不同位置所获得涂层的形貌及微观结构进行了表征,并研究了沉积速率、表面形貌、微观结构及堆积缺陷的变化规律。
采用PAS烧结工艺在1680℃成功制备出SiC-石墨复相陶瓷,并研究了石墨含量对复相陶瓷物理力学性能、韧性、R曲线(阻力曲线)行为和抗热震性能的影响。结果 表明:随着石墨含量的增加复相陶瓷的致密度、抗弯强度、弹性模量和维氏硬度均有所降低;以韧化比(TI)作为复相陶瓷的韧性指标,表明石墨含量越多,复相陶瓷的韧性越好,存在陡峭的上升R曲线行为,该指标更能反映复相陶瓷的韧性特征;显微形貌分析发现,复相陶
The nanostructured MoO2/rGO/Ni foam 3-dimentional electrode for supercapacitor is synthesized via a two-step method.First, the graphene oxide (GO) prepared by Hummers method is electrodeposited on nic
会议
Sandwich structure composites were prepared by aluminum foam and basalt fiber, ultra-high molecular weight polyethylene(UHMWPE) fiber composite faceplate.The factors influencing the impact properties
Silicon carbide coatings were fabricated by chemical vapor deposition method using domestic graphite as substrate and methyltrichlorosilance as precursor.Two frock design: drum type and steamer type,
SiC-graphite ceramic composites were successfully fabricated by plasma activated sintering (PAS) method at 1680 ℃.The effects of graphite content on the physical mechanical properties, toughness, R-cu
Lithium-Zinc ferrite hollow microspheres (LiZn FHMs) doped with La, Mg were synthesized by Fe+Zn+Fe2O3+O2+Li2CO3 reactive system based on self-reactive quenching technology.Influence of La, Mg doping