Viscosity is one of the most important metallurgical properties of ironmaking slags.In the present study,the viscosities of SiO2-CaO-Al2O3-MgO based slags containing minor elements,including Na2O,K2O,
【机 构】
：
The University of Queensland,Brisbane,Australia S
【出 处】
：
第十届中国钢铁年会暨第六届宝钢学术年会
论文部分内容阅读
Viscosity is one of the most important metallurgical properties of ironmaking slags.In the present study,the viscosities of SiO2-CaO-Al2O3-MgO based slags containing minor elements,including Na2O,K2O,FeO,CaF2,B2O3,CaS,TiO2 and MnO have been systematically studied.The viscosities of synthetic slags with the additions of minor elements have been measured using the rotational rheometer at high temperature.After viscosity measurement,the sample was quenched,mounted,polished and analysed by electron probe micro-analysis.It was found that all of minor element additives will decrease the slag viscosity.The ability to reduce the viscosity can be ranked as CaF2> B2O3 > CaS > Na2O >K2O > TiO2 > MnO > FeO.Based on the present measurements and available viscosity data from literatures,a viscosity model was proposed to describe the viscosity of SiO2-CaO-Al2O3-MgO based slags containing minor elements.The model predictions were found to have an outstanding agreement with the experimental data at blast furnace(BF)slag composition range.The present work will improve the understanding of the behaviours of BF slags with inclusion of minor elements.The viscosity model developed will be used for industrial process optimization.
其他文献
通过对雅矿尾砂矿石性质的物相分析,确定了一磁—磨矿—分级—二磁的选矿工艺,通过实验室流程试验,确定了流程工艺参数.当磨矿粒度为-0.074mm占86％,磁场强度为105kA/m时,通过单一磁选实验室流程试验取得了最终品位51.84％,回收率62.93％,产率62.93％的良好指标.
The mixtures of nitric acid and hydrofluoric acids are typically utilized for the pickling process of stainless steel.However,with the increasing environmental and safety consciousness due to nitrates
In modern iron blast furnace operations,utilising low grade iron ores and poor quality fuels is essential for low cost ironmaking.The accurate information of phase equilibria for complex slag system i
气液两相流广泛存在于炼钢连铸工艺过程中，如复吹转炉冶炼、底吹氩气钢包冶炼、吹氩式浸入式水口、中间包气幕挡墙等，研究气泡的运动规律有助于揭示冶金反应过程中潜在的本质规律。通过物理实验,研究了压强、底吹流量对气泡形状、尺寸、数量及“渣眼”尺寸的影响,研究表明:随着底吹流量增加,高压条件下的气泡比常压条件下的气泡更趋向于正圆形,气泡直径平均值变小,气泡数量增多,气泡形状和直径在底吹流量为4L/h时变化最
In the field of stainless steel flat product cold rolling,the 20-Hi mill has clearly proved its technological superiority compared to other rolling mill types such as 6-High rolling mill or split hous
研究和实施了电磁场在铜合金棒、铜及铜合金管和铜合金板带坯水平连续铸造中的应用,获得了高质量的铸坯.例如,采用非真空水平电磁连续铸造的高强高导Cu-Cr-Zr铸坯制备的高铁用接触导线的平均拉强度610MPa,导电率79.85％IACS,批量应用于京沪高铁,2010年10月3日在京沪高铁线通过了最高运营时速486.1公里的实验.
High temperature slags could act as not only heat carrier and catalyst but also reactants in some chemical reactions to produce syngas due to the individual components in slags.A new method is put for
为了提高0.6mmDX51D+Z通卷力学性能均匀性,对热轧卷进行了提高头尾卷取温度即U形卷取试验.利用带钢力学性能在线检测设备EMG-IMPOC,对0.6mmDX51D+Z通卷力学性能进行检测,根据头尾与中部的力学性能差异来设定U形卷取工艺.对实施U形卷取工艺前后的DX51D+Z头、中、尾力学性能进行了对比.采用金相显微镜对碳化物形貌进行观察,采用试样电解和ICP方法对AlN析出物数量进行检测,对
针对汽车用高强无间隙原子钢(IF钢),采用德国Zwick HTM16020高速拉伸试验机对实验钢在应变速率为10s-1、100s-1、400s-1、800s-1下进行高速拉伸实验,得到应力应变曲线,对其变形行为进行了分析.结果表明:与准静态拉伸相比,高速拉伸下170P1钢的强度、塑性等力学性能均发生明显的变化,在高速拉伸下屈服强度和抗拉强度均大于准静态时.随应变速率的增大实验钢的断后延伸率先增大后
With ever increasing demand to reduce cost and environmental impact,more tinplate producers are looking to switch away from Phenol Sulfonic Acid(PSA)based electrolytes.The tried and tested choice when