【摘 要】
：
本文将长碳纳米管(CNT)分散于水中,利用聚乙烯吡咯烷酮(PVP)或自聚合多巴胺(PDA)的辅助作用,通过真空抽滤法制备出CNT,CNT/PVP,CNT/PDA,CNT/PVP/PDA等薄膜.与CNT,CNT/PVP
【机 构】
：
中国科学院苏州纳米技术与纳米仿生研究所 215123
【出 处】
：
第二届中国国际复合材料科技大会 (CCCM-2)
论文部分内容阅读
本文将长碳纳米管(CNT)分散于水中,利用聚乙烯吡咯烷酮(PVP)或自聚合多巴胺(PDA)的辅助作用,通过真空抽滤法制备出CNT,CNT/PVP,CNT/PDA,CNT/PVP/PDA等薄膜.与CNT,CNT/PVP,CNT/PDA相比,CNT/PVP/PDA薄膜表现出良好的性能.PVP与PDA的协同效应通过透射电镜、紫外可见光光谱及拉曼光谱进行表征,结果表明,在CNT/PVP/PDA体系中CNT不仅通过PVP分散,还通过PDA相互粘结.
其他文献
In this study, poly (lactic acid) (PLA)-based composites were prepared by solution blending method using nano-sized calcium carbonate (nano-CaCO3) and nano-
In order to obtain high-performance composites with high vibration damping, we prepared three-dimensional graphene foam reinforced epoxy composites, and inv
Barium hydroxide octahydrate possesses a larger mass heat storage capacity among low temperature phase change materials.Its latent heat is 264kJ/kg, and its
Poly (β-hydroxybutyrate-co-β-hydroxyvalerate) (PHBV) has been widely used in potential applications due to its biodegradation, biocompatibility, piezoelec
碲(Te)化物纳米线因为其优异的热电性质在热电器件领域应用前景广阔，引起了学者的广泛关注。对于碲化物纳米线的制备及形貌控制方面的研究成为该领域研究的热点。本研究采
Carbon Nanotube (CNT) FloTube9100 manufactured by CnanoTechnology will be adopted, Hydroxyl have been successfully attached by functionalizing the surface o
为获得具备优异粘弹阻尼特性的高性能复合材料，以表面生长石墨烯的泡沫镍为模板，制备石墨烯/泡沫镍/环氧树脂混杂复合材料，并对其静态力学性能、动态粘弹性能以及振动阻尼特
随着电子业和通讯业的发展，场发射平板显示器已经渗入人们的生活中，这无疑对场发射平板显示产品的核心结构场发射阵列有很大的要求，但应用最多的硅尖锥场发射阵列的基底材料
本文将多壁碳纳米管(Multiwalled nanotubes,MwNTs)薄膜埋入环氧树脂复合材料,对环氧树脂复合材料的破坏行为进行了在线监测研究。结果 发现,通过合理铺层设计,在预定破
芽孢杆菌从中国工业微生物菌种保藏管理中心(CICC)选择用来沉积MgHPO4· 1.2H2O和Mg3 (PO4)2·5H2O.通过粉末X-ray衍射(XRD)、扫描电镜(SEM)和透射电镜(TEM)、傅里叶红外