【摘 要】
:
In-situ generated MgAl2O4 nanowhiskers reinforced 6061 aluminum (Al) alloy composites have been successfudly synthesized by reaction hot pressing under a relatively low temperature (600 ℃).
【机 构】
:
Tianjin Key Laboratory of Composite and Functional Materials,School of Materials Science and Enginee
【出 处】
:
The 11th China-Japan joint conference on Composite Materials
论文部分内容阅读
In-situ generated MgAl2O4 nanowhiskers reinforced 6061 aluminum (Al) alloy composites have been successfudly synthesized by reaction hot pressing under a relatively low temperature (600 ℃).
其他文献
对ELID砂轮氧化膜中吸附水及晶格水的存在进行了理沦分析与实验研究,提出 ELID磨削氧化膜中吸附水与晶格水的二步冷却机理,进一步提出ELID磨削温度模型,并进行了理论计算。研究表明,ELID氧化膜中存在吸附水与晶格水,由于吸附水和晶格水的冷却作用,ELID磨削温度模型计算结果偏低于传统磨削温度模型,该结果对ELID磨削有利。
Mechanochemistry is emerging as unique technology for polymer processing including composite fabrication..Its application to cellulose attracts special attention due to the materials abundance and uti
W-30wt.%Cu and TiC-50wt.%Ag were successfully synthesized by a novel simplified pretreatment followed by electroless plating.The 0 wt.%TiC,0.5 wt.%TiC,and 0.5wt.%TiC--0.5wt,%Ag composite powders were
The purpose of this study is to investigate how affect the hot needle punching on inter-laminar fracture toughness of CFRTP.
The aim of this study is to increase the friction coefficient between.C/C composites at low temperature to moderate the dependence of the frictional coefficient on the temperature condition.
Carbon fiber sandwich structures,with higher specific stiffness,specific strength,energy-absorbed ability,fatigue resistance and thermal functions,have been widely used in aerospace,automotive,marine
该论文综述了负热膨胀系数(NTE)材料和负膨胀纤维强化复合材料。论述了高强UHMW-PE纤维Dyneema和PBO纤维Zylon的细微结构、分子结晶取向及刚性直线分子链的桥原子横向热振动,及由此引起的纤维负膨胀机理。讨论了负膨胀纤维强化复合材料的性能和制备。最后介绍了负膨胀纤维强化复合材料在超导线轴上的应用。
采用光还原法制备出SrTiO3-石墨烯复合光催化剂.利用XRD,FTIR,TEM和紫外-可见漫反射光谱对样品进行了表征.结果表明:SrTiO3纳米颗粒均匀地附着在石墨烯表面,复合样品的带隙约为3.35 eV.
纤维增强陶瓷基复合材料在拉伸载荷作用下,其应力-应变曲线会出现明显的非线性行为,基体开裂、纤维/基体界面脱粘和纤维断裂等损伤机制是其出现非线性的主要原因.采用细观力学方法建立了预测纤维增强陶瓷基复合材料拉伸应力-应变曲线的模型.采用剪滞模型描述复合材料出现损伤后的细观应力场,通过损伤模型确定拉伸载荷下细观损伤参量的演化,将剪滞模型与损伤模型相结合,预测了纤维增强陶瓷基复合材料单轴拉伸应力-应变曲线
聚合物基软磁性复合材料以其耐热性能好、耐腐蚀、韧性好、易加工和相对密度低等优点而被广泛应用于电子技术、通讯、汽车、航天航空等诸多领域。本文采用环氧树脂WSR-615和AG-80为基体,以Fe-Si磁性颗粒为填料,通过热压成型方法制备了高含量软磁性树脂基复合材料,并对复合材料的热性能、力学性能和磁性能进行了研究。