An Al-1.08 vol.% Si alloy was cold rolled to a reduction of 98% (εvM =4.5) and then annealed at different temperatures up to 250 ℃ for different times.The morphologies of the Si particles were charact
【机 构】
:
College of Materials Science and Engineering, Chongqing University, China
【出 处】
:
15th International Conference on Aluminium Alloys(ICAA15)(第十
论文部分内容阅读
An Al-1.08 vol.% Si alloy was cold rolled to a reduction of 98% (εvM =4.5) and then annealed at different temperatures up to 250 ℃ for different times.The morphologies of the Si particles were characterized and their effects on the microstructure and mechanical properties of the deformed and annealed samples were investigated.The deformed structure is characterized by a nanoscale lamellar structure with the presence of Si particles of coarse (> 1 μm), medium (100 nm-1 μm) and fine (< 100 nm) sizes in the matrix.The fine Si particles are aligned along the lamellar boundaries indicating a stabilizing effect on the structural refinement during cold rolling.
其他文献
We report on our latest results on high efficiency n-type metal-wrap-through (MWT) cell and module technology.The bifacial n-type MWT cells are produced using industrial processes in industrial full-s
Mono-like crystalline silicon ingot with high purity was continuously casted with metallurgical-grade silicon (MG-Si) as feedstock.Our advanced electron beam melting (EBM) system is able to effectivel
Solar simulators copy the AM1.5 spectrum for an accurate efficiency measurement of solar cells.Encapsulation of solar cells with EVA and glass modify the AM1.5 spectrum inside the module.Less UV light
本文对定向凝固(DSS)法生长的P型掺硼多晶硅材料的太阳电池片的关照衰减问题,采用不同的光致衰减方法,对太阳能电池片电性能的影响进行了简单的对比研究,可以再次验证其中一种方法在行业中的普遍应用,可以通过比较两种衰减方法,保证太阳能电池片输出电性能的稳定、准确与可靠性,给使用单位建议可行的衰减方式。
With increased market demand for distributed solar array systems, module makers and installers are looking forward to the solutions of easy installation and cost effective.Based on DuPont performance
Bifacial photovoltaic devices, thanks to their proven benefits and the maturity of the production processes, can make a breakthrough in the photovoltaic market.However, the current lack of standardize
Some advanced crystalline silicon solar cells and modules technologies present evolutions of their backside metallisation.This results in new needs in terms of non-permanent contacting for characteriz
The thermal laser separation (TLS) allows the ablation free cleaving to separate solar cells with a high edge quality.The process is based on thermal induced mechanical stress, generated by a well-adj
Current modules and systems lose a significant part of their power when shade is present.A solution is presented by adapting the electrical lay-out of the module, without additional manufacturing cost
Electron beam melting (EBM) system has been used to improve the purity of metallurgical grade silicon (MG-Si) feedstock for photovoltaic application.Our advanced EBM system with the combination of vac