掺钕离子的钒酸钇晶体(Nd:YVO4)是适合于激光二极管(LD)泵浦较为理想的固体增益介质之一.但Nd3+离子半径大(0.1109nm),Y3+离子半径小(0.1019nm),在生长过程中用Nd3+取代Y3+离子时,将引起YVO4正方晶格畸变趋向,导致晶体中出现结构应力,出现小角晶界缺陷,从而?
Nd: YVO4 doped neodymium ion is one of the ideal solid gain media for laser diode (LD) pumping. However, Nd3 + has a large radius (0.1109nm) and a small Y3 + ion (0.1019nm). When Nd3 + is substituted for Y3 + in the growth process, the distortion of the square lattice of YVO4 will be induced, resulting in the structural stress in the crystal with a small angle Grain boundary defects, thus?