【摘 要】
：
At present commonly used techniques for fabricating anode substrates are tape-casting,extrusion molding and slip casting.Generally,tape-casting[1] and extrusion molding[2] are used to fabricate planar
【机 构】
：
School of Chemistry and Chemical Engineering.,South China University of Technology.,Guangzhou,Guangd
论文部分内容阅读
At present commonly used techniques for fabricating anode substrates are tape-casting,extrusion molding and slip casting.Generally,tape-casting[1] and extrusion molding[2] are used to fabricate planar and straight tubular anode for mass production.They are not suitable for preparing the products with complex shape.
其他文献
Polymer Electrolyte Membrane Fuel Cells (PEMFCs) are one of the most promising alternative energy systems with wide applications in transportation,stationary and portable electronic devices.However,Pt
以磷酸(PA)掺杂聚苯并咪唑(PBI)膜为电解质的质子交换膜燃料电池,运行工作温度高达120-200 oC,近年来备受研究者的青睐.与以全氟磺酸膜为电解质工作温度在80 oC左右的质子交换膜燃料电 池相比具有以下技术上的优势,包括:较高的CO耐受能力,简化的水管理系统,更有效的热利用,一体化的燃料处理系统和电池系统等.
以水作为溶剂,乙二醇为还原剂,氢氧化钠、硝酸铈以及氯铂酸溶液为前驱体,通过简单 的溶剂热法成功合成出了Pt 含量为20wt.％的Pt/CeO2-C 催化剂.相比于其他方法,本方法只需一步 溶剂热实验过程以及随后的热处理过程,方法简单、制备出的催化剂性能较好.
质子交换膜燃料电池(PEMFC)的制造成本居高不下,限制了其商业化发展.以Pt 为壳 层的M@Pt(M 为Co,Ni,Cu 等过渡金属)核壳结构催化剂在降低Pt 载量、提高催化剂活性 等方面表现出良好的性能,已成为燃料电池领域的研究热点.
The novel cobalt,nitrogen-codoped octahedral carbon (Co-N-OC) non-precious metal catalyst was synthesized by heat treatment of a cobalt (II) complex under nitrogen atmosphere.Similarly,Ni-N-OC and Zn-
2V/0.4Ah ultra-battery has been assembled with Cabot electrode and Heda active carbon electrode respectively,and then the ultra-batteries are subjected to a variety of tests,such as charge acceptance,
Electrochemical capacitors,also called supercapacitors,have drawn considerable attention recently because of their high power density,ultrafast charge-discharge rates and ultralong cycling lifespan,wh
过渡金属氧化物/纳米碳复合材料超电容性能的研究在近20年来受到广泛关注.为了使得所组装的超级电容器具有更高的比能量,需使器件不储能材料所占重量比较低,即应采用氧化物载量高的复合材料和厚膜电极.然而,文献报道常为低氧化物负载量和薄膜电极.本文研究高载量氧化钌包覆碳纳米管复合材料的制备及其厚电极超电容性能.
随着社会的发展,可利用的能源不断告急,开发新能源刻不容缓.直接醇燃料电池由于 具有原料来源广,污染低,方便储存、运输等诸多的优点而别广泛的研究应用[1].但是,目 前金属催化剂的催化活性低及价格昂贵,催化剂载体的选择及大规模生产等问题阻碍了燃料 电池大批量的投入商业生产.
二氧化钛在酸碱溶液中具有良好的稳定性,且价格较为低廉,在燃料电池中可作为金属 催化剂的载体,提高电催化活性,其中阳极氧化制备的二氧化钛纳米管(TiO2 nanotubes,TiO2 NTs)容易控制纳米管的生成,比表面积大并具高抗腐蚀性,以及较强的吸附性,被认为是 有可能取代碳载体的电极材料1.本文利用电沉积的方法将铂负载在二氧化钛纳米管电极表 面,发现电沉积的铂的电催化活性会受热处理影响.