Cracking Behavior in Additively Manufactured Pure Tungsten

来源 :金属学报(英文版) | 被引量 : 0次 | 上传用户:pingli_lp
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
In this study,near fully dense (96.5%) pure tungsten bulks were additively manufactured and the cracking behavior was investigated.A crack network with a spacing of ~ 100 μm was observed in the fabricated bulks.It was observed that the laser scanning strategy,which could tailor the microstructure,affected the crack distribution pattern in fabricated tungsten.The calculated surface temperature difference (7300 K) was much higher than the cracking criterion (800 K) of tungsten,indicating that cracking is almost inevitable in laser additive manufacturing of tungsten.It could be concluded that crack network formed because the cracks emerged in every laser molten track and then interconnected in the layer-by-layer building process.
其他文献
The application and component designs of single crystal superalloys are restricted by the precipitation of topologically closed packed (TCP) phases,which can deteriorate the microstructural stability of the alloys severely.Limited researches concerning th
In as-welded state,each region of 2219 aluminum alloy TIG-welded joint shows different microstructure and microhardness due to the different welding heat cycles and the resulting evolution of second phases.After the post-weld heat treatment,both the amoun
The cooling curves and the change of contraction/expansion during solidification and cooling were tested by using a selfmade device which could achieve the one-dimensional contraction instead of three-dimensional contraction of the casting.Then,the effect
The microstructure and mechanical properties of the as-cast and heat-treated Mg-4.6Y-2.5Zn-0.6Zr-xSn (x =0,0.2 and 0.5 wt%) alloys were investigated in this work.The results showed that the eutectics have been refined with 0.2% Sn addition and it has no e
Previous studies showed that significant increases in elongation in Mg-Ce alloys due to the Ce addition and the solute drag effect by Ce addition were ascribed to the non-basal dislocation slip activating and the texture altering.The microstructure evolut
The Mg MB26/Al 7075 composite rod,in which Mg MB26 serves as the sleeve and Al 7075 serves as the core,is fabricated via the process of co-extrusion.The influence of extrusion speed on the microstructure evolution,interface bonding and mechanical response
Aiming at the requirements of structural steel in Gen-IV nuclear reactor,the high-chromium martensitic heat-resistant steels containing 10-12% chromium were developed.The toughness of heat-affected zones (HAZs) is one of the important factors for evaluati
In the present study,the weld formation and mechanical properties of the AA-5A06 friction pull plug welded (FPPW) joints were improved by controlling the axial force history.Several defect-free FPPW joints were made successfully by using the welding param
A 17 vol% SiCp/Al-Mg-Si-Cu composite plate with a thickness of 3 mm was successfully friction stir welded (FSWed) at a very high welding speed of 2000 mm/min for the first time.Microstructural observation indicated that the coarsening of the precipitates
In the present experimental investigation,Al-3 wt%Cu and A1-3 wt%Cu-0.5 wt%Mg alloys castings are produced by a horizontal solidification technique with a view to examining the interrelationship among growth rate (GR),cooling rate (CR),secondary dendrite