【摘 要】
：
In as-welded state,each region of 2219 aluminum alloy TIG-welded joint shows different microstructure and microhardness due to the different welding heat cycles and the resulting evolution of second phases.After the post-weld heat treatment,both the amoun
【机 构】
：
Department of Mechanical Engineering, Tsinghua University, Beijing 100084, China;China Academy of La
论文部分内容阅读
In as-welded state,each region of 2219 aluminum alloy TIG-welded joint shows different microstructure and microhardness due to the different welding heat cycles and the resulting evolution of second phases.After the post-weld heat treatment,both the amount and the size of the eutectic structure or θ phases decreased.Correspondingly,both the Cu content in α-Al matrix and the microhardness increased to a similar level in each region of the joint,and the tensile strength of the entire joint was greatly improved.Post-weld heat treatment played the role of solid solution strengthening and aging strengthening.After the post-weld heat treatment,the weld performance became similar to other regions,but weld reinforcements lost their reinforcing effect on the weld and their existence was more of an adverse effect.The joint without weld reinforcements after the post-weld heat treatment had the optimal tensile properties,and the specimens randomly crack in the weld zone.
其他文献
The high-current pulsed electron beam (HCPEB) treatment with current density 6 J/cm2 was applied on AZ91 Mg alloy to improve its corrosion resistance.Results showed that the net-like Mg17Al12 disappeared on the surface of AZ91 Mg alloy after irradiation b
The effect of lead on the initial corrosion behavior of 316LN stainless steel has been investigated by U-bend immersion experiments in 4 wt％ NaOH solutions at 300 ℃.Follow-up studies after soaking were carried out by scanning electron microscope,energy di
In this work,the effect of prior cold deformation on the stability of retained austenite in GCr15 bearing steel was investigated after quenching and tempering treatment.The thermal stability was evaluated by calculating thermal activation energy for decom
Mg AZ31/Al 7050 laminate was fabricated by co-extrusion directly from the as-cast Mg AZ31 and Al 7050 billets.The influence of annealing temperature and annealing time on microstructure and mechanical behavior of the extruded Mg/Al laminate was systematic
The AZ31 Mg alloys were processed by 6％ pre-compression and frustum shearing extrusion at various temperatures,and the microstructure,texture and mechanical properties of the resulting alloys are systematically investigated.The results show that the grain
The rupture behavior of the modified 10Cr-lMo steel multi-layer welded joint is determined by the fine-grain zones of the weld metal adjacent to the fusion line during the long-term creep test at 620 ℃.The microstructures of multi-layer weld metal before
The tensile creep behavior of extruded Mg-6Gd alloy,having the tensile yield strength of ～ 110 MPa at 175 ℃,has been investigated under 175 ℃ and 150 MPa.In this study,the extruded Mg-6Gd sample exhibits the total tensile strain of ～ 10.5％ after the creep
The influences of heat treatment and test condition on the microstructure and stress rupture properties of a Ni-Mo-Cr-Fe base corrosion-resistant superalloy have been investigated in this paper.Optical microscope and scanning electron microscope were empl
Enhancing combinatorial properties,such as excellent corrosion resistance,high strength and good ductility combined,is an important issue for manufacturing high-quality AlMgSi(Cu) alloys.Here,we show that this can be achieved by optimizing a combinatorial
The application and component designs of single crystal superalloys are restricted by the precipitation of topologically closed packed (TCP) phases,which can deteriorate the microstructural stability of the alloys severely.Limited researches concerning th