【摘 要】
：
报道了YBCO粉末与Ag基带复合轧制Ag-YBCO复合超导带的制备工艺、显微结构和超导性能。用带Ag基带的粉轧工艺已制备出YBCO层厚度为10μm、与Ag基带结合牢固的Ag-YBCO复合带。
【机 构】
：
西北有色金属研究院,西北有色金属研究院,西北有色金属研究院
论文部分内容阅读
报道了YBCO粉末与Ag基带复合轧制Ag-YBCO复合超导带的制备工艺、显微结构和超导性能。用带Ag基带的粉轧工艺已制备出YBCO层厚度为10μm、与Ag基带结合牢固的Ag-YBCO复合带。扫描电镜观察发现,YBCO层中晶粒较致密,但晶粒形貌却与一般烧结块差不多。在流动氧气中于920℃/12小时热处理后,复合带最高临界电流密度J_c(77K、0T、1μV/cm判据)值达6300A/cm~2。
The preparation, microstructure and superconductivity of Ag-YBCO composite superconducting tape were reported. Ag-YBCO composite tape with YBCO layer thickness of 10μm and strong bond with Ag substrate has been prepared by powder rolling process with Ag substrate. Scanning electron microscopy showed that the grains in YBCO layer were denser, but the grain morphology was similar to that of ordinary sintered ones. The maximum critical current density J_c (77K, 0T, 1μV / cm criterion) of the composite tape reached 6300A / cm ~ 2 after heat treatment in flowing oxygen at 920 ℃ for 12 hours.
其他文献
在(Nd,Fe)(76.5)Co_(15)Al_1B_(7.5)的基础上,研究丁Nd,Fe量变化对合金性能的影响,其形式为Nd_(18-x)Fe_(58.5+x)Co_(15)Al_1B_(7.5),x=1,2,3,4,结果合金最佳性能出现在Nd量
本文通过测定塑化曲线确定聚乙烯(PE)的毛细管挂丝温度范围,测试了挤出原丝和低温区域拉伸丝的力学性能和热收缩行为。结果表明,低压下的毛细管挤出工艺对 PE 丝的力学性能影
该文对制备高Jc Bi—2223/Ag带均匀的长样进行了研究。为了提高长样的均匀性,我们采取了如下的工艺:(a)用预烧结块料灌银管;(b)每道用大变形量轧制;(c)缓慢升温以便主要生成2
本文讨论静载荷及疲劳载荷作用下 C/Al 正交层压板的力学响应,并考虑损伤过程中的临界现象,以此作为结构设计准则的基础。对静载荷作用的情况:(1)90°铺层的门槛应变ε_(FPF)
研究了非晶态Ce_2Fe_(23)B_3合金的晶化以及亚稳态化合物Ce_2Fe_(23)B_3的结构与磁性XRD分析证实,Ce_2Fe_(23)B_3为bcc结构,晶格常数α=1.417nm由Ce_2Fe_(23)B_3的室温Mossba
语文课堂教学的有效性是语文教学的生命,而这生命能否得以延续,取决于教师是否能充分发掘学生的兴趣点,调动学生学习的主动性和积极性,能否做到与文本有机结合,真情演绎文本
研究了锰对 Cu-Zn-Al 形状记忆合金的 Tβ(x+β/β)点、晶粒度、相变温度和形状恢复率的影响。研究结果表明 Cu-Zn-Al 合金中添加少量锰,可以降低 Tβ点、细化晶粒、降低相变
有效的数学学习活动不是单纯的依赖模仿与记忆,而是借助生生之间、师生之间的有效对话,构建起自主探索与合作交流的数学学习方式。在课堂教学中,怎样去挖掘知识,发现规律以及
在新形势和新课改的背景下,小学数学的教育不能够再采取直接灌输知识给学生的教学方式了。为了提高小学生学习数学的能力,教师必须要让小学生懂得去主动学习数学,并学会探索
教师是学校发展的关键,只有教师的发展和完善,才能促进学生的发展和完善。基于这样的认识,我们努力探索小学语文教师发展的管理模式,构建教师培训的长效机制,采取短期培训和