Nickel leaching from low-grade nickel matte (LGNM) using aqueous ferric chloride solution was studied.The influence of factors such as leaching temperature and
【机 构】
：
School of Metallurgy, Northeastern University, Shenyang 110819, China
论文部分内容阅读
Nickel leaching from low-grade nickel matte (LGNM) using aqueous ferric chloride solution was studied.The influence of factors such as leaching temperature and concentration of ferric chloride on the nickel leaching ratio was investigated.The results show that increasing leaching temperature and concentration of ferric chloride increases the nickel leaching ratio.The overall nickel leaching process follows the unreacted shrinking core model,and the surface chemical reaction is the rate-controlling step.The activation energy and the reaction order of the nickel leaching process,controlled by the surface chemical reaction,were calculated to be 52.96 kJ.mo1-1 and 0.5,respectively.Therefore,the kinetics equation for the nickel leaching was found to be 1-(1-α)1/3 =7.18 × 104C0.5exp[-52,960/(RT）]t.
其他文献
The bulk Ti-6Al-4V alloy was hydrogenated at the temperature range of 723-973 K,and the hydrogen absorption characteristics and hydrogen absorption kinetics wer
The lithium-ion capacitor is a promising energy storage system with a higher energy density than traditional supercapacitors.However,its cycling and rate perfor
Microstructures of Cu-4.7Sn (％) alloys prepared by two-phase zone continuous casting (TZCC) technology contain large columnar grains and small grains.A compound
The hot deformation behavior of Al-Cu-Li alloy was investigated by hot compression tests in the temperature range of 340-500 ℃ with strain rate of 0.001-10.000
The defect-free CoCrNbNiW high-entropy alloy coating was successfully prepared by laser melting deposition,and its microstructure and wear resistance were inves
The Bi0.5Sb1.4-xNaxIn0.1Te3 (x =0.02-0.20) alloys were fabricated by high vacuum melting and hotpressing technique.The phase structures and morphology of the bu
Ultrafine rare-earth oxides (REOs) are widely applied in all fields of daily life,but the conventional preparation methods are limited by a long procedure,low e
Cu matrix composite materials reinforced with B4C particle at four different contents (1.5 wt％,3.0 wt％,4.5 wt％ and 6.0 wt％) and also CuAl matrix composites with 13
调查了湖南省内石煤开发生产链中几家典型企业——石煤发电厂、炼钒厂、煤渣制砖厂的辐射环境现状,监测了厂内及其周边的γ辐射剂量率、~(222)Rn浓度以及尾渣、渣砖、土壤、水中放射性核素含量,初步确定了这些环境物质中的放射性水平,评估了其对环境的影响,提出了治理和预防放射性污染的措施。