Several action regimes were employed, namely, those exposed to solutions containing single and/or composite chloride and sulfate salts, and under wet-dry cycles and/or flexural loading. The variations in dynamic modulus of elasticity(Erd values) were monitored, as well as the key factor impacting on the chloride ingress when concrete subjected to multiple action regimes was identified by the method of Grey Relation Analysis(GRA). The changes in micro-structures and mineral products of interior concrete after different action regimes were investigated by means of X-ray diffraction(XRD), mercury intrusion technique(MIP), and scanning electron microscopy(SEM). The test results showed that the cyclic wet-dry accelerated the deterioration of OPC concrete more than the action of 35% flexural loading based on the results of Erd values and the GEA. The analyses from micro-structures could give certain explanations to the change in Erd values under different action regimes. Several action regimes were employed, namely, those exposed to solutions containing single and / or composite chloride and sulfate salts, and under wet-dry cycles and / or flexural loading. The variations in dynamic modulus of elasticity (Erd values) were monitored, as well as the key factor impacting on the chloride ingress when concrete by multiple action regimes was identified by the method of Gray Relation Analysis (GRA). The changes in micro-structures and mineral products of interior concrete after different action regimes were investigated by means of X-ray diffraction (XRD), mercury intrusion technique (MIP), and scanning electron microscopy (SEM). The test results showed that the cyclic wet-dry accelerated the deterioration of OPC concrete more than the action of 35% flexural loading based on the results of Erd values ​​and the GEA. The analyzes from micro-structures could give certain explanations to the change in Erd values ​​under different action regimes.