提出了20碳钢的最佳退火工艺,即将退火温度限定在710℃进行退火。这种热处理工艺,在改善低碳钢冲压成形方面,具有良好效果。
The optimal annealing process of 20 carbon steel is proposed, that is, the annealing temperature is limited to 710 ℃ for annealing. This heat treatment process, in improving low-carbon steel stamping, with good results.