对载银氧化镁 (MgO)在不同温度下烧结 ,用XRD ,SDT对样品进行了测试分析 ,结果表明 :载银氧化镁中银的含量随着烧结温度的升高而逐渐减少 ,烧结温度到 132 0℃时 ,银的含量几乎为零 ,给载银氧化镁抗菌陶瓷烧结温度的选择提供了依据
The results show that the content of Ag in silver-loaded magnesia decreases with the increase of sintering temperature, and the sintering temperature reaches 132 At 0 ℃, the content of silver is almost zero, which provides a basis for the selection of silver-doped magnesium oxide anti-bacterial ceramic sintering temperature