In this paper, spring steel-60Si2Mn and stainless steel-1Cr18Ni9Ti were rolled one pass in the semi-solid state. The microstructural evolution during rolling of
【机 构】
：
Department of Metal Forming
论文部分内容阅读
In this paper, spring steel-60Si2Mn and stainless steel-1Cr18Ni9Ti were rolled one pass in the semi-solid state. The microstructural evolution during rolling of the steels with different solid fraction was investigated. The experimental results showed that the manner of liquid and solid phases flowing and deforming was different. During rolling, most of solid phases remained in the center of the rolled specimens, while liquid phase flowed to the edge, which resulted in the macrosegregation of liquid and solid phases. Only the amount of solid fraction reached a certain value, were the solid phases deformed and flattened.
其他文献
Al62.5Cu25Fe12.5 alloy was prepared by arc melting. It was found that the formation of quasicrystalline phase is related to the condition of annealing, such as
A new superstructure form of heat exchanger networks (HEN) is proposed based on expert system (ES).The new superstructure form is combined with the practical en
The manner by which the particles settle in the laminar flow region is first described and the characteristics of co-sedimentation of two-species particles are
The bonding of steel plate to Al-7graphite slurry was studied for the first time. The relationship model about preheat temperature of steel plate,solid fraction
The synthesis and characterization of a series of novel poly(aryl amide imide)s based on o-diphenyltrimellitic anhydride are described.The poly(aryl amide-imide
The structure characteristics of ID precision ultrathin monocrystalline silicon section cutting machine-tool spindle with force-monitoring bearings functioning
AIM: Matrix metalloproteinase-1 (MMP-1) and tissue inhibitor of matrix metalloproteinase-1 (TIMP-1) are central to the spontaneous resolution of liver fibrosis.
An Al-50wt%TiC composite was directly synthesized by self-propagating high-temperature synthesis (SHS) technology,and then was used as a grain refining master a
In this study, Cu was added as the third additive to lower the sintering temperature of W-Ni-Fe alloy. By adding 2 wt pct Cu, a dense 93W-3.5Ni-1.5Fe-2.0Cu tung
The effect of the melt superheating temperature on the as-cast microstructure of a cast nickel-base superalloy M963 has been investigated. The results show that