测定了1500℃时磷在BaO-CaO-Na2O-CaF2-Cr2O3渣子和0.12C-0.7Si-18Cr不锈钢熔体之间的分配比。试验结果表明,该渣系的不锈钢脱磷能力比CaO基渣好,与BaO基渣相当。
The distribution ratio of phosphorus between BaO-CaO-Na2O-CaF2-Cr2O3 slag and 0.12C-0.7Si-18Cr stainless steel melt at 1500 ℃ was measured. The test results show that the slag system of stainless steel dephosphorization capacity is better than CaO-based slag, and BaO-based slag equivalent.