采用动态硫化法以双2,5过氧化物为硫化剂制备了PA6/POE-g-MAH热塑性弹性体。结果表明,当硫化剂用量为POE-g-MAH质量分数的1.5%~2.5%,PA6的质量分数为35%~50%时,制备的试样具有最佳的力学性能。
The PA6 / POE-g-MAH thermoplastic elastomer was prepared by dynamic vulcanization using double 2,5 peroxide as vulcanizing agent. The results show that when the amount of curing agent is 1.5% ~ 2.5% of POE-g-MAH and the content of PA6 is 35% ~ 50%, the prepared samples have the best mechanical properties.