Mesoporous materials with the highest surface area were synthesized by hydrothermal treatment from coal-measure kaolin using cetyltrimethylammonium bromide(CTAB)as template.The effect of several factors on surface area of products also had been discussed.The products were characterized by FT- IR,HRTEM and N 2 adsorption and desorption isotherm plot methods.There was typical structure as Si-O,Si- OH and Si-O-Si of mesoporous materials in the framework of synthesized materials;the pore size distributions of the products showed a sharp peak at 3.82 nm.The effect of hydrothermal treatment time and the amount of template on the specific surface area of mesoporous materials was important,when the Surf/Si=0.135,and hydrothermal time=12 h,and the surface area of the product reached up to 1 070 m2/g,which was higher than other products.
Mesoporous materials with the highest surface area were synthesized by hydrothermal treatment from coal-measure kaolin using cetyltrimethylammonium bromide (CTAB) as template. The effect of several factors on surface area of products also had been discussed. The products were characterized by FT-IR, HRTEM and N2 adsorption and desorption isotherm plot methods. There was typical structure as Si-O, Si-OH and Si-O-Si of mesoporous materials in the framework of synthesized materials; the pore size distributions of the products showed a sharp peak at 3.82 nm. The effect of hydrothermal treatment time and the amount of template on the specific surface area of mesoporous materials was important, when the Surf / Si = 0.135, and hydrothermal time = 12 h, and the surface area of the product reached up to 1 070 m2 / g, which was higher than other products.