【摘 要】
：
A series of CaMoO4 phosphors doped with trivalent dysprosium ions (Dy3+) and lithium (Li+) were prepared by solid state method at 750 ℃ for 3 h. X-ray diffract
【机 构】
：
College of Physics Science and Technology
论文部分内容阅读
A series of CaMoO4 phosphors doped with trivalent dysprosium ions (Dy3+) and lithium (Li+) were prepared by solid state method at 750 ℃ for 3 h. X-ray diffraction (XRD) confirmed the crystal structure and quality of phosphors. Scanning electron microscopy (SEM) indicated that the phosphors presented good crystalline state, and the crystalline grain sizes were about 0.5-3.0 μm. The emission spectra showed that the phosphors had intense emission at 480 (4F9/2→6H15/2), 576 (4F9/2→6H13/2) and 660 nm (4F9/2→6H11/2). Meanwhile, the excited spectra indicated it had intense excitation at 352 (6H15/2→6P7/2), 390 (6H15/2→4M21/2) and 450 nm (6H15/2→4I15/2). As a charge compensator, Li+ ions were incorporated into CaMoO4:Dy3+ phosphors, which enhanced the PL intensities depending on the doping concentration of Li+. The optimal molar fraction of Dy3+ ions in Ca1-xMoO4:xDy3+, 0.05Li+was 0.05.
其他文献
The mutual destabilization between complex hydrides and lithium amide has been comprehensively reported. In this paper, CeH2 doped Li-Mg-N-H/NaA1H4 composite wa
The effects of Ce, Y and Gd additions on the as-cast microstructure and mechanical properties of Mg-3Sn-lMn alloy were investigated and compared by using optica
轻型纸是一种纸质疏松、表面平滑、印刷性能好的印刷用纸。采用西康80/48阔叶木化机浆替化针叶木化机浆生产轻型纸,产品具有强度好,平滑度高,成本下降等特点。纸的松厚度,经
酶在制浆造纸工业中的应用,从20世纪80年代中期起迅速发展起来。化学浆的磨浆或打浆是生产纸及纸板极为关键的工段。分析了打浆酶预处理对漂白针叶木浆(NBKP)和漂白阔叶木浆(
The structure and high-temperature electrochemical properties of the as-cast and annealed (940 ℃, 8 h) La0.60Nd0.15Mg0.25Ni3.3Si0.10 hydrogen storage alloys we
We reported on the successful synthesis of the Nd:YAG (Nd:Y3Al5O12) nano-powders by using urea as the precipitant with the microwave assisted homogeneous precip
纸张通常有定量稳定,厚薄适中,布浆均匀,内在、外观质量良好的要求。介绍了采用纸张的定量、厚度、均匀度的自动监控技术,实施生产、技术管理,对确保产品质量,提高生产效率,
The self-assembly of 5-bromoisophthalic acid (H2BIPA) with Eu(NO3)3·6H2O under the hydrothermal conditions gave a 3D coordination polymer, Eu2(BIPA)3(CH3CH2OH)
The full densification polycrystalline cerium hexaboride (CeB6) cathode material was prepared by using the spark plasma sintering (SPS) method in an oxygen free
Y3MnxFe4.85-xO12 (x=0, 0.02, 0.04, 0.06, 0.08 and 0.1) garnet ferrites (YMnlG) were prepared by conventional solid-state reaction method in air atmosphere. The