【摘 要】
：
生产真空铬铁所需要的高碳碳素铬铁(C≥7.5%,Si≤1.2%,Cr≥65%,S≤0.04%),我广原用易熔铬矿冶炼。我们曾几次用难熔或比较难熔铬矿试炼高碳碳素铬铁,均未获得满意的结果。为
论文部分内容阅读
生产真空铬铁所需要的高碳碳素铬铁(C≥7.5%,Si≤1.2%,Cr≥65%,S≤0.04%),我广原用易熔铬矿冶炼。我们曾几次用难熔或比较难熔铬矿试炼高碳碳素铬铁,均未获得满意的结果。为了满足真空铬铁生产的需要,我厂组织技术攻关小组,再次进行了用难熔铬矿生产高碳碳素铬铁的试验,并取得了较好的结果。
The production of high-carbon carbon ferrochrome required for vacuum ferrochromium (C ≥ 7.5%, Si ≤ 1.2%, Cr ≥ 65%, S ≤ 0.04%), I Kwong-yuan smelting with easy-melting chrome ore. We have tried the high carbon carbon ferrochrome several times with refractory or refractory chrome ore, but we have not obtained satisfactory results. In order to meet the needs of vacuum ferrochromium production, our factory organized a technical research group to carry out the trial of producing high-carbon ferrochromium with refractory chrome ore again and achieved good results.
其他文献
7月汇总水泥企业382家,生产水泥7629.54万吨,与去年同期比增长6.16%,增加442.63万吨;累计水泥产量45010.67万吨,同比增长1.45%,比去年同期增加642.22万吨。本月销售水泥7714.
观测原发性肝癌患者经肝动脉化疗栓塞（ＴＡＥ）＋３２Ｐ内照射治疗后免疫功能状态改变。方法检测２３例ＴＡＮ＋３２Ｐ治疗后原发性肝癌患者和２０例健康献血员血液可溶性白细胞介素２受体（ｓＩＬ－２Ｒ）、辅助Ｔ淋巴细胞、抑制Ｔ淋巴细胞
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
鞍钢六号高炉(炉容1050米~3)在1976年大修中,修建了三座AWR-Ⅰ型热风炉,设计风温为1250～1300℃,并在拱顶和高温区选用硅砖。本文通过对六高炉硅砖热风炉三年多生产实践的总结,
电子工业的迅速发展,对磁性材料提出了越来越高的要求。特别是电子器件的小型化与集成化,要求材料在更高的频率下使用。为此,用粉末冶金方法研制出Ni80Mo4高频磁粉芯。本文
1病例报告患者，男，56岁，教师，因近1个月来出现口渴多饮、多尿、多食、乏力，无上腹痛及恶心呕吐等消化道症状。到医院门诊查空腹血糖及餐后2小时血糖分别为8．Zmmol／L、15．Zmmol／I，，尿糖（m），
近年来,由于溶剂萃取的应用,铜的湿法冶金得到了很大发展。随着露天采矿范围的增大和矿石品位的下降,湿法炼铜在铜冶炼中所占的比例将日益增加。在我国许多矿山和冶炼厂的坑
本文采用有限元素法求解二维稳定温度埸,应用迭代技术确定炉底1150℃等温线位置,提供了一种计算高炉炉底温度分布的有效方法。编制了计算程序。并就几种不同衬里条件的炉底温
设有中间漏斗的旋转布料器被认为是当前性能较好的一种布料器。本文叙述了中间漏斗对改进旋转布料器的性能所起的作用,并对中间漏斗的几何参数、转速及驱动功率进行了分析研
由于冶炼高温合金的需要,我厂于1972年开始生产高钒铁。随着生产的发展,高钒铁标准逐渐提高,由协议标准发展为企业标准,后由我厂提出制定了冶金部标准,1980年我厂又制定了赶