【摘 要】
：
The effect of Cu on the microstructure and mechanical properties of 2519 aluminum alloy was investigated by means of tensile test, microhardness test, transmiss
【机 构】
：
School of Materials Science and Engineering
论文部分内容阅读
The effect of Cu on the microstructure and mechanical properties of 2519 aluminum alloy was investigated by means of tensile test, microhardness test, transmission electron microscopy, and scanning electron microscopy. The results show that when the content of Cu is less than 6.0%, the strength of 2519 aluminum alloy increases with the increase of Cu content; when the content of Cu is more than 6.0%, the strength of the alloy decreases.The hardening effect of the aged alloy is accelerated at 180 ℃ and the time to peak age is reduced, but the plasticity of the alloy gradually decreases with the increase of Cu content. However, the hardening effect of the aged alloy decreases with the increase of Cu as the content of Cu is over 6.0%. The optimal content of Cu of 2519 aluminum alloy is 6.0%, at which the alloy has best tensile strength and plasticity.
其他文献
TC4 titanium alloy was welded by double-sided gas tungsten arc welding(GTAW) process in comparison with conventional GTAW process, the microstructure and mechan
Gold nanoparticles dispersed Y2O3 films were prepared through a sol-gel method by using yttrium acetate and Au nanoparticles colloid as precursors. The films we
A continuous loading push-out test technique was used to measure the interfacial shear strength of SiC fiber reinforced Ti matrix composites. The interracial sh
An ever increasing demand for zinc has resulted in worldwide efforts to exploit complex and lean grade reserves of zinc oxide ore. In this study experiments wer
Er3+:Y0.5Gd0.5VO4 crystal with good optical quality was grown by Czochraski method. The structure of the crystal was determined by X-ray powder diffraction meth
A numerical model Alloy/M has been applied to investigate the microsegregation in Al-4.45 wt pct Cu alloy. The calculated data were compared with the experiment
The measurements of temperature dependence of the magnetic susceptibility of La1-xSrxCoO3 perovskite oxides at different Sr doping (0≤x≤0.5) and annealing tem
The feasibility of forming pollution-free and environmentally benign Ce-based rare earth conversion coatings (short for RECCs) on AZ91 magnesium alloy to enhanc
A new forming process, ceramic matrix composites thixoforming in pseudo-semi-solid state, was proposed based on powder metallurgy technology combined with the s
The vacuum-free vibration liquid phase(VLP) diffusion-bonding of SiCp/ZL101A composites was investigated. The effects of vibration on the interface structure, t