以(NH2)2Mo7O24.4H2O为钼源,CS(NH2)2为硫源和还原剂,采用水热法合成纳米二硫化钼,研究了不同酸度对产物的影响。通过XRD、SEM、EDS对产物进行表征。结果表明:酸度对纳米二硫
论文部分内容阅读
以(NH2)2Mo7O24.4H2O为钼源,CS(NH2)2为硫源和还原剂,采用水热法合成纳米二硫化钼,研究了不同酸度对产物的影响。通过XRD、SEM、EDS对产物进行表征。结果表明:酸度对纳米二硫化钼层状结构的形成和发育以及晶化程度和产物的粒径和微观形貌有显著影响;当反应体系中pH=2时,可通过该法合成结晶良好,纯度较高,粒径约为280 nm的“球花”状2H-MoS2。
(NH2) 2Mo7O24.4H2O as molybdenum source and CS (NH2) 2 as sulfur source and reductant. Hydrothermal synthesis of nano-MoS2 was carried out to study the effect of different acidity on the product. The product was characterized by XRD, SEM, EDS. The results show that the acidity has a significant effect on the formation and development of the nanostructured molybdenum disulfide layered structure and the degree of crystallization and the particle size and the morphology of the product. When the pH value is 2 in the reaction system, High purity, particle size of about 280 nm “Bulb ” 2H-MoS2.
其他文献
分别采用固相法和共沉淀法工艺制备了不同Ag掺杂量的La2/3Sr1/3MnO3∶Agx(LSMO∶Agx,x为摩尔百分比,x=0.00、0.10、0.20、0.30、0.40)多晶材料,通过XRD和R-T对La2/3Sr1/3MnO3
介绍了电解液喷射沉积制备泡沫金属技术,说明了电解液喷射沉积法的原理及特点,综述了泡沫镍在电极材料、催化剂载体和超级电容器等方面的应用。
The technology of spray me
利用热分析天平,采用动态连续称重法分别对M5和Zr-4合金在380、400℃水蒸气条件下进行氧化试验,分析其氧化动力学规律,并利用扫描电镜观察氧化层形貌.结果表明:在380、400℃
研究了硫对Ni-Cr-W-Al高温合金热塑性的影响.结果表明,当硫含量(质量分数)为0.0004％时,在950～1250℃时,合金的热塑性很好,面缩值都在55％以上；随着硫含量的增加,热塑性不断降低,当
采用真空高频磁悬浮炉制备出一系列Gd3Al2-xSix(x=0,0.1,0.2,0.5,0.8)合金。通过Si对Al的部分替代,研究了Si元素微量替代对Gd3Al2合金磁热效应的影响。结果表明,Gd3Al2-xSix
采用雾化-双辊急冷法和热挤压工艺,制备了快速凝固/粉末冶金Mg-6wt%Zn-5wt%Ca合金,研究了合金在150～200℃和压力为30～70MPa的压缩蠕变行为。结果表明,随温度和应力的升高,合金
将Cu、In粉均匀混合后放入刚玉管式真空炉中热烧结3 h制备Cu-In合金,烧结温度950℃。将制备好的Cu-In合金研磨成粉后再与Se粉均匀混合,把得到的均匀混料再次放入刚玉管式真空
研究了α+β两相区变形时不同应变量下,TC21合金的微观组织演变过程及拉伸性能变化规律。结果表明,应变量对初生α相的形态有显著影响;随应变量的增大,初生α相的形态由短棒
综述了一维纳米金属氧化物纳米材料的常用制备方法,并在此基础上进一步阐述了ZnO纳米管、纳米线,TiO2纳米管和Al2O3纳米线的性能与制备。介绍了其他几种纳米氧化物的研究现状
为增强铝青铜的抗腐蚀性能,通过激光熔覆技术在表面熔覆一层镍基合金熔覆层,通过静态腐蚀试验、电化学腐蚀试验、微观组织分析、扫描电镜等方法及腐蚀机理分析,对比QA19-4铝