Helium-containing Ti films are prepared using magnetron sputtering in the helium-argon atmosphere. Isochronal annealing at different temperatures for an hour is employed to reveal the behaviour of helium bubble growth. Ion beam analysis is used to measure the retained helium content. Helium can release largely when annealing above 970 K. A thermal helium desorption spectroscopy system is constructed for assessment of the evolution of helium bubbles in the annealed samples by linear heating (0.4K/s) from room temperature to 1500K. Also, Doppler broadening measurements of positron annihilation radiation spectrum are performed by using changeable energy positron beam. Bubble coarsening evolves gradually below 680K, migration and coalescence of small bubbles dominates in the range of 680-970K, and the Ostwald ripening mechanism enlarges the bubbles with a massive release above 970K.