论文部分内容阅读
The effects of different annealing conditions on the phase formation with NaZn13 structure were investigated in La(Fe1–xCox)11.9Si1.1 (x=0.068) compounds. It was found that the 1:13 phase was not formed directly from the melt upon cooling but via a perite