The influence of carbon content on the stacking fault energy(SFE)of Fe-20Mn-3Cu twinning-induced plasticity(TWIP)steel was investigated by means of X-ray diffraction peak-shift method and thermodynamic modeling.The experimental result indicated that the stacking fault probability decreases with increasing carbon addition, the SFE increases linearly when the carbon content in mass percent is between 0.23% and 1.41%.The thermodynamic calculation results showed that the SFE varied from 22.40to 29.64mJ·m-2 when the carbon content in mass percent changes from 0.23%to 1.41%.The XRD analysis revealed that all steels were fully austenitic before and after deformation,which suggested that TWIP effect is the predominant mechanism during the tensile deformation process of Fe-20Mn-3Cu-XC steels.
The influence of carbon content on the stacking fault energy (SFE) of Fe-20Mn-3Cu twinning-induced plasticity (TWIP) steel was investigated by means of X-ray diffraction peak-shift method and thermodynamic modeling. The experimental result indicated that the stacking coefficient probability decreases with increasing carbon addition, the SFE increases linearly when the carbon content in mass percent is between 0.23% and 1.41%. The thermodynamic calculation results showed that the SFE varied from 22.40 to 29.64 mJ · m-2 when the carbon content in mass percent changes from 0.23% to 1.41%. XRD analysis revealed that all steels were fully austenitic before and after deformation, which suggested that TWIP effect is the predominant mechanism during the tensile deformation process of Fe-20Mn-3Cu-XC steels.