Nafion modified Pt nano-particles with size about 4nm were synthesized.The modified particles were absorbed on the surface of carbon nanotubes and used as electro-catalysts for proton exchange membrane fuel cell. Due to the plentiful proton channels provided by the modifying Nafion ionomers, the single fuel cell with the modified Pt catalyst has a promised performance. The output was 0.282W/cm2 with Pt loading of 0.1mg/cm2, better than that of unmodified one, which was 0.273W/cm2 with Pt loading of 0.11mg/cm2.
Nafion modified Pt nano-particles with size about 4nm were synthesized. The modified particles were absorbed on the surface of carbon nanotubes and used as electro-catalysts for proton exchange membrane fuel cell. Due to the plentiful proton channels provided by the modifying Nafion ionomers, the single fuel cell with the modified Pt catalyst has a promised performance. The output was 0.282 W / cm2 with Pt loading of 0.1 mg / cm2, better than that of unmodified one, which was 0.273 W / cm2 with Pt loading of 0.11 mg / cm2.