论文部分内容阅读
Bi_2O_3-ZnO-B_2O_3 system glass is a kind of lead-free low melting sealing glasses. The structure of Bi_2O_3-ZnO-B_2O_3 system low-melting sealing glass was investigated by DSC, FT-IR, XRD and SEM. The results show that with the increase of B_2O_3 content, the transition temperature Tg and softening temperature T_f of Bi_2O_3-ZnO-B_2O_3 system low-melting sealing glasses increase, which leads to the liquid phase precipitation temperature increasing and promotes the structure stability in the glass. With increasing the heat treatment temperature, a large number of liquid phases appear in samples and the sinter efficiency of the samples increases. The FT-IR spectra of the glasses show the presence of some bands that are assigned to vibrations of Bi-O bond from [BO_3] pyramidal and [BiO_6] octahedral units and B-O from [BO_3] and [BO_4] units. With the decrease of B_2O_3 content, the crystallization tendency of the glass increases. In glass samples B_1 and B_2, crystallization starts at 460 ℃ and 540 ℃, respectively. Both of them precipitate Bi-(24)B_2O_(39) phases.