目的研制用于大气再生技术Sabatier二氧化碳还原反应的低温催化剂 ,以降低Sabatier反应的起动温度。方法从催化剂活性组分、载体的选择、催化剂的制备方法和条件等方面进行低温催化剂的设计研制 ,建立催化剂性能测试装置 ,对低温催化剂的性能进行实验研究。结果研制了以钌为催化剂活性组分 ,以活性r Al2 O3为载体的Sabatier反应低温催化剂 ,其反应起动温度可降到 1 1 0℃ ,起动时间 8min ;在温度为 2 0 0~ 30 0℃时 ,贫组分一次通过转化率均高于 95% ;产物水较为纯净 ,无色透明 ,呈中性。结论Sabatier反应低温催化剂的性能达到了设计目的 ,有进一步研究的价值。
Aim To develop a low temperature catalyst for the Sabatier carbon dioxide reduction of atmospheric regeneration to reduce the onset temperature of Sabatier reaction. Methods The design and development of low temperature catalysts were carried out from the aspects of catalyst active components, carrier selection, catalyst preparation methods and conditions, and the catalyst performance testing device was established to study the performance of low temperature catalysts. Results A low-temperature catalyst for Sabatier reaction with ruthenium as active component and active r Al 2 O 3 as carrier was prepared. The reaction start-up temperature was reduced to 110 ℃ and the start-up time was 8 min. At a temperature of 200 ~ 300 ℃ When the lean components passed the conversion rate were higher than 95%; product water more pure, colorless and transparent, was neutral. Conclusion The performance of the Sabatier reaction at low temperature catalyst has achieved the design goal and has the value of further research.