【摘 要】
:
Quantum chemical calculation was carried out to choose a promoter which can reduce the poisoning of V2O5/TiO2 catalysts by SO2. Several atoms were chosen as can
【机 构】
:
Metal Processing Research Center Korea Institute of Science and Technology Cheongryang Seoul 130-65
论文部分内容阅读
Quantum chemical calculation was carried out to choose a promoter which can reduce the poisoning of V2O5/TiO2 catalysts by SO2. Several atoms were chosen as candidates and new catalysts were synthesized by impregnation method. The NOx conversion rate was measured at temperatures between 100 and 400 ℃ and poisoning effect was investigated. The most promising candidate promoter, Se, was excluded because of its high vapor pressure. On the other hand, Sb shows best promoting properties. Sb promoted catalyst reaches the maximum NOx conversion rate at 250 ℃. It also shows considerably enhanced resistance to poisoning of V2O5/TiO2 catalysts by SO2.
Quantum chemical calculation was carried out to choose a promoter which can reduce the poisoning of V2O5 / TiO2 catalysts by SO2. Several atoms were chosen as candidates and new catalysts were synthesized by impregnation method. The NOx conversion rate was measured at temperatures between 100 and 400 ℃ and poisoning effect was investigated. The most promising candidate promoter, Se, was excluded because of its high vapor pressure. On the other hand, Sb shows best promoting properties. shows considerably enhanced resistance to poisoning of V2O5 / TiO2 catalysts by SO2.
其他文献
The polymer-ceramic composites of epoxy resin (EP) and barium titanate (BT) were prepared.BT powders of different BT particle sizes from 100 nm to 1 μm were us
The ranking problem is studied when the pairwise comparisons values are uncertain in the analytic hierarchy process (AHP). The method of constructing the judgme
The nanocrystalline Bi2O3-Y2O3 solid electrolyte material was synthesized by pressureless reactive sintering process with Bi2O3 and Y2O3 nano mixed powder as ra
The improvements of microstructures and properties of a high strength aluminum cast alloy were studied.The effects of rare earth elements on the microstructures
The effects of hot pressing on electric performance and mechanical strength of Bi0.5Sb1.5Te3 thermoelectric material prepared through vacuum melting and milling
The effects of NiO on microstructure and magnetic properties of Mn-Zn ferrite with a nominal composition of Zn0.32Mn0.60-xNixFe2.08O4 were investigated. The cal
In order to control the size and distribution of the high conductive Fe2P in LiFePO4/Fe2P composite, two different cooling rates (Fast: 15 ℃·min-1, Slow: 2 ℃
A line shaped electron beam recrystallised polycrystalline silicon film on the low cost substrate was investigated for the use of the solar cell absorber. The a
Essential oil, with more than thirty kinds of compounds separated and identified by gas chromatographymass spectrometry, was extracted from Shatian shaddock pee