The effects of NiO on microstructure and magnetic properties of Mn-Zn ferrite with a nominal composition of Zn0.32Mn0.60-xNixFe2.08O4 were investigated. The cal
【机 构】
：
State Key Laboratory of Electronic Thin Films and Integrated Devices,Jiangsu Research Center of Magn
论文部分内容阅读
The effects of NiO on microstructure and magnetic properties of Mn-Zn ferrite with a nominal composition of Zn0.32Mn0.60-xNixFe2.08O4 were investigated. The calcined powder of Mn-Zn ferrite was characterized by X-ray diffraction (XRD), the fracture surface of Mn-Zn ferrite was checked by scanning electronic microscope (SEM), and then the magnetic properties were measured. As a result, the substitution of Ni can cause the crystallattice constant of MnZn ferrite to decline, and the grain size to decrease, therefore improve the magnetic performance of MnZn ferrite whose density exceeds 5.0 g·cm-3.
其他文献
Cu-Zn, Cu-Zn-Sn, Cu-Zn-Ni alloys were melted by vacuum smelter. The effect factors to the surface free energy of the alloys such as chemical composition, crysta
An electromagnetic anti-fouling technology(EAFT) was developed further. The operating principle of the EAFT was presented using fundamental physics laws. To val
Based on the moving least-square (MLS) approximation, the complex variable moving least-square approximation (CVMLS) is discussed in this paper. The complex var
The equation of stress intensity factors(SIF) of internally pressurized thickwalled cylinder was used as the reference case. SIF equation of rotating thick-wall
The polymer-ceramic composites of epoxy resin (EP) and barium titanate (BT) were prepared.BT powders of different BT particle sizes from 100 nm to 1 μm were us
The ranking problem is studied when the pairwise comparisons values are uncertain in the analytic hierarchy process (AHP). The method of constructing the judgme
The nanocrystalline Bi2O3-Y2O3 solid electrolyte material was synthesized by pressureless reactive sintering process with Bi2O3 and Y2O3 nano mixed powder as ra
The improvements of microstructures and properties of a high strength aluminum cast alloy were studied.The effects of rare earth elements on the microstructures
The effects of hot pressing on electric performance and mechanical strength of Bi0.5Sb1.5Te3 thermoelectric material prepared through vacuum melting and milling