对浙江省开化林场9年生无性系杉木和实生苗杉木木材的物理力学性质进行了测定比较。结果表明,在测定的15个无性系中,有的优于实生苗杉木,有的次于实生苗杉木。无性系杉木材的平均气干密度为0340g·cm-3,基本密度0280g·cm-3,径向干缩系数0131%,弦向干缩系数0217%,体积干缩系数0401%,抗弯强度44355MPa,抗弯弹性模量8296GPa,冲击韧性32950kJ·m-2。
The physical and mechanical properties of 9-year-old clonal fir and seedling fir woods in Kaihua Forest Farm of Zhejiang Province were measured and compared. The results showed that among the 15 clones tested, some were better than the seedling fir and some were secondary to the seedling fir. The average air-dry density of clonal fir wood was 0340g · cm-3, the basic density was 0280g · cm-3, the radial shrinkage coefficient was 0131%, the chord-wise shrinkage coefficient was 0217% The shrinkage coefficient is 0401%, the flexural strength is 44355MPa, the flexural modulus is 8296GPa, the impact toughness is 32950kJ · m-2.