A series of 3.0Mo/MCM-22-Al2O3 catalysts with γ-Al2O3 contents in the range of 0-100 wt%were prepared and applied in the metathesis reaction of ethene and butene-2.Addition of γ-Al2O3 did not affect the structure of MCM-22 zeolite as evidenced by XRD and N2 adsorption measurements.It was deduced from TPR experiments that γ-Al2O3 phase favored the formation of polymolybdate or multilayered Mo oxide,while more Al2(MoO4)3 species were generated over MCM-22 zeolites.Alumina content in the support was directly related to the metathesis activity of ethene and butene-2 to propene.Mo species with higher valence(Mo6+or Mo5+)contributed more to the excellent performance of catalyst than metallic Mo.The best catalyst activity and stability was obtained over 3.0Mo/(MCM-22-30%Al2O3)under the reaction condition of 1.0 MPa and 125℃ using N2 as the pretreatment gas.
A series of 3.0Mo / MCM-22-Al2O3 catalysts with γ-Al2O3 contents in the range of 0-100 wt% were prepared and applied in the metathesis reaction of ethene and butene-2.Addition of γ-Al2O3 did not affect the structure of MCM-22 zeolite as evidenced by XRD and N2 adsorption measurements. It was deduced from TPR experiments that γ-Al2O3 phase favored the formation of polymolybdate or multilayered Mo oxide, while more Al2 (MoO4) 3 species were generated over MCM-22 zeolites. Aluminum content in the support was directly related to the metathesis activity of ethene and butene-2 to propene. Mo species with higher valence (Mo6 + or Mo5 +) contributed more to the excellent performance of catalyst than metallic Mo.The best catalyst activity and stability was obtained over 3.0Mo / (MCM-22-30% Al2O3) under the reaction condition of 1.0 MPa and 125 ° C using N2 as the pretreatment gas.