The martensite structure in Cu-25Al-3Mn alloy and its thermal cycling and aging behavior are studied. It is convinced that the M2H martensite can be obtained by water-quenched, and the atoms distribution on the basal plane of the mart ensite is: Ⅰ(corner)-Al; Ⅱ(center of the plane)-Cu; Ⅲ(middle of b- side)-22/25Cu+3/25Mn. The lattice parameters are determined to be a=0.445 9 nm, b=0.527 9 nm, c=0.424 1 nm, β=88.64°. The triangle and other complicated configurations consisting of the variant group in the martensite are discovered. It is showed that the tested alloy has a high thermal stability when aging at average temperature in the parent phase, and the thermoelastic martensite amount is up to 90% af ter aging for 96 hat 400 ℃. The thermal cycling has a little influence on the transform ation temperature (Ms). When the number of thermal cycles is up to 1000, the increasing of Ms is only 8 ℃.