【摘 要】
:
The novel felt-metal supported PVA composite hydrophilic ultrafiltration membrane was used for the treatment of oil/water(O/W) emulsion. The effects of transmem
【机 构】
:
School of Chemistry and Chemical Engineering,School of Metallurgical Science and Engineering
论文部分内容阅读
The novel felt-metal supported PVA composite hydrophilic ultrafiltration membrane was used for the treatment of oil/water(O/W) emulsion. The effects of transmembrane pressure(TMP), cross flow velocity, feed concentration on membrane performance were investigated, and ultrasonic cleaning of the fouled membrane was also investigated. The results show the flux increases with the increase of cross-flow velocity and TMP within the given TMP range from 0.20 MPa to 0.40 MPa. With increase of initial oil concentration increases, the oil rejection increases while the permeate flux decreases. The composite membrane shows more than 90% oil rejection within the initial oil concentration range from 0.05% to 0.50% (mass fraction) at TMP of 0.30 MPa. The fouling of the composite membrane increases rapidly during the initial 20 min at given TMP range from 0.20 MPa to 0.40 MPa, and it increases slowly after 30 min. The results also show that ultrasound is very effective in removing oil fouling of the fouled membrane, and the properties of the composite ultrafiltration membrane can be completely recovered by 10 min of sonication.
其他文献
Laves phase NbCr2 alloys with a composition of Nb-66.7Cr (molar fraction, %) were prepared by mechanical alloying and hot pressing. The microstructures and prop
Epitaxial YBCO superconducting films were deposited on the single crystal LaAlO3. (001) substrate by metal organic deposition method. All YBCO films were fired
The phosphor BaB8O13:Eu3+ were synthesized by solid-state reaction, and their luminescent properties were studied under 254 and 147 nm excitation. The excitatio
The amenability of a refractory ore to the extraction of gold and silver by cyanide leaching was investigated. Diagnostic leaching tests were also performed to
The isothermal oxidation behavior of a Ti3Al-based alloy (Ti-24Al-14Nb-3V-0.5Mo-0.3Si, molar fraction, %) at 700- 1 000 ℃ in air was investigated. The oxidatio
The separation techniques of vanadium and molybdenum were summarized, and a new method of removal V(Ⅴ) from Mo(Ⅵ) by adsorption with chelate resin was present
Numerical control(NC) bending experiments with different process parameters were carried out for 5052O aluminum alloy tubes with outer diameter of 70 mm, wall t
Ceramic LaNiO3 samples were prepared by solid state reaction method at different sintering temperatures. It was found that the resultant was not ABO3 perovskite
In recent times, conventional materials are replaced by metal matrix composites (MMCs) due to their high specific strength and modulus.Strength reliability, one
The alloys were prepared in Mg-rich corner of Mg-Zn-Ce system. Partial phase equilibrium relationships of these alloys at 350 ℃ were identified by using scanni