【摘 要】
:
Hydroisomerization of linear alkanes to branched isomers is an important petrochemical process for production of gasoline with high octane number.Non-noble meta
【机 构】
:
State Key Laboratory of Heavy Oil Processing,China University of Petroleum,Qingdao 266580,China;EMS
论文部分内容阅读
Hydroisomerization of linear alkanes to branched isomers is an important petrochemical process for production of gasoline with high octane number.Non-noble metal bifunctional catalysts used in this process always suffer from low metal dispersion and poor metal-acid synergy.Herein,a facile one-pot synthesis method was used to simultaneously regulate metal particle sizes and acidity of the Ni-SAPO-11 hydroisomerization catalyst.The physicochemical properties are investigated using XANES,EXAFS,TEM/STEM,FT-1R,XPS,UV-vis and NH3-TPD.Apart from the highly dispersed nickel nanoparticles with an average diameter of 8 nm,the framework Ni2+ions are generated via substituting framework Al3+ions of the SAPO-11.The formed NiP-OH structures have lower deprotonation energy(DPE)than the SiAl-OH ones,contributing more and stronger acid sites to the Ni-SAPO-11 catalyst.The great metal-acid synergy including high metal to acid sites ratio(nNi/nA)and close intimacy is obtained for the Ni-SAPO-11 catalyst.The Ni-SAPO-11 catalyst outperforms the counterpart prepared by the impregnation method and exhibits comparable activity and isomers selectivity to the Pt/SAPO-11 catalyst in the n-hexane hydroisomerization.
其他文献
A nanocrystalline CoCrFeNiMn high-entropy alloy(nc-HEA)with nano-multiphase structure was pre-pared by inert gas condensation(IGC)using a laser evaporation sour
A novel equimolar high-entropy(HE)transition metal monoboride,(Cr0.2Mn0.2Fe0.2Co0.2Mo0.2)B,was designed and prepared in powder and bulk form by high temperature
The undercooling dependence of the solidification mechanism was systematically explored by the elec-trostatic levitation(ESL)facility.During the experiments,the
Laser aided additive manufacturing(LAAM)was used to fabricate bulk Fe49.5Mn30Co10Cr10C0.5 interstitial multicomponent alloy using pre-alloyed powder.The room te
The synergistic effects of area ratio and microstructure on the galvanic corrosion of A508/309 L/308 L dissimilar metals weld(DMW)are studied by a multi-analytical approach.It was demonstrated that decreasing the anode/cathode surface area ratio obviously
Construction of metal-organic-frameworks-based composite photocatalysts has attracted much atten-tion for the reasonable band gap and high surface areas to impr
2D transition metal dichalcogenides(TMDs)have been considered as promising non-precious electrocatalysts for the hydrogen evolution reaction(HER).However,their limited active sites and poor electric conductivity pose a significant hurdle to their HER perf
In a solution treated Co-20Ni-6Si shape memory alloy,coherent nano-particles were precipitated after annealing at 873 K for 1 min,but the shape memory effect al
Thin film capacitors with excellent energy storage performances,thermal stability and fatigue endurance are strongly desired in modern electrical and electronic
To gain insight into the ageing behavior of ultrafine grain(UFG)structure,the precipitation phenom-ena and microstructural evolutions of Mg-6Zn-1Y-0.4Ce-0.5 Zr(